The effect of pH values on the properties of ceria-zirconia oxygen storage material synthesized by coprecipitation-reflux method

Yong ZHENG,Guohui CAI,Ying ZHENG,Yihong XIAO,Lilong JIANG

DOI: https://doi.org/10.3969/j.issn.1001-9731.2017.07.017

2017-01-01

Abstract:A series ceria-zirconia solid solution oxygen storage materials were successfully synthesized by coprecipitation-reflux method.The reflux treatment of freshly precipitated cerium-zirconium hydroxides was carried out in a teflon flask.Effect of the pH of the precipitated solution on the synthesis of ceria-zirconia solid solution oxygen storage materials was studied.The samples were characterized by X-ray diffraction, N2 physical adsorption and hydrogen temperature programmed reduction.The results show that by controlling the pH of the precipitated solution at about 11, the obtained sample exhibited the best properties.After calcination at 600 ℃ for 5 h, it not only has a high surface area approaching to 91.1 m2/g, a narrow pore radius size distribution centered on around 3.9 nm, and a pore volume of 0.22 m3/g, but also has the lowest reducible temperature with the total oxygen storage capacity up to 309 μmol/g.Furthermore, after calcination at 1 100 ℃ for 5 h, the samples still have a single phase, which indicates its high thermal stability.