Effects on compound oxygen storage materials of calcinations temperature

LIU Ping,ZHAO Ming,FANG Hua,GONG Mao-chu,CHEN Yao-qiang
DOI: https://doi.org/10.3969/j.issn.1004-1656.2007.05.011
2007-01-01
Abstract:In the present paper,Ce-Zr-Y-La-Mn oxygen storage material was synthesized by co-precipitation method and characterized by X ray diffraction(XRD),BET,TG and temperature programmed reduction(TPR).The effects of textural and structural properties,low temperature redox behavior,and change in phase were investigated at various calcination temperatures.The XRD results show that the samples belong to the same crystalline shift at various calcinations temperature and the fluorite structure of the precipitation keeps unchanged.The new phase is not separated from the solid solution after calcined at 1000℃.The BET results show that the surface area of the sample reaches 45m2/g after aging 5h at 1000℃.The TPR results show that the sample indicates best reducibility calcined at 600℃.