Abstract:The nanostructures and redox properties of CeO2-ZrO2 materials can be tuned via optimized thermal treatments. In this study, the CeO2-ZrO2-Y2O3-La2O3 (CZ) materials were prepared by co-precipitation method and submitted to different thermal treatment conditions (atmosphere: nitrogen (N) and air (A); temperature (x): 700, 800 and 900 degrees C). Due to the protective effects of the "in-situ-formed" carbon powder, treating the surfactants assisted-CZ precursors under N2 atmosphere can keep the pore struc-tures and then the CZ-N70 0 and CZ-N80 0 can achieve larger surface area than CZ-A70 0 and CZ-A80 0, respectively. In comparison, with high treatment temperature (900 degrees C), the effects of thermal atmo-sphere on surface area can be ignored. However, the redox properties of CZ materials correlate closely with thermal treatment atmosphere and temperature simultaneously. As demonstrated by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) characterizations, the N2 atmosphere fa-cilitates the formation of Ce3 thorn without disturbing the mixing degree of Ce and Zr. Thereby the CZ-Nx materials exhibit superior reducibility than corresponding CZ-Ax materials. In addition, the XRD and XPS results also demonstrate the formation of a more homogeneous CZ solid solution by Zr atoms rear-rangement with temperature ignoring the atmosphere. As a result, the reducibility of CZ materials in-creases with the treatment temperature increasing and is not affected by the worsening of the textural properties. Specially, due to the synergistic effects of N2 atmosphere and high treatment temperature, the CZ-N90 0 shows the best reducibility. This improvement also emphasizes the important role of structural properties of CZ in explaining the temperature-dependent reducibility.(c) 2022 Chinese Society of Rare Earths. Published by Elsevier B.V. All rights reserved.

Effects of Thermal Treatment Conditions on Redox Properties of Ceria-Zirconia Materials

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Effect of Ce/Zr Atomic Ratio on the TWC Properties of PdO/CexZr1-xO2(x=0-1.0) Catalysts

Effect of Preparation Method on the Surface and Redox Properties of Ce0.67zr0.33o2 Mixed Oxides

Effects of co-precipitation temperature on structure and properties of La and Y doped cerium zirconium mixed oxides

The influence of H2O2 on the properties of CeO2-ZrO2 mixed oxides

Improving the Comprehensive Properties of ZrO2–C Materials with Aid of TiO2 Addition

Effect of Yttrium Doping on Oxygen Storage Capacity of Ce_(0.33)Zr_(0.67)O_2

Significant Improvement of Thermal Stability for CeZrPrNd Oxides Simply by Supercritical CO2 Drying

Modification of CeO2–ZrO2 Mixed Oxides by Coprecipitated/impregnated Sr: Effect on the Microstructure and Oxygen Storage Capacity

Chemical expansion of La 3+ and Yb 3+ incorporated Zr-doped ceria ceramics for concentrated solar energy-driven thermochemical production of fuels

Effect of doping CeO2 and Sc2O3 on structure, thermal properties and sintering resistance of YSZ

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

Effect of temperature-dependent nano SiC on the ablation resistance of ZrC coating

Enhanced Thermal Stability and Oxygen Storage Capacity for CexZr1-xO2 (x = 0.4−0.6) Solid Solutions by Hydrothermally Homogenous Doping of Trivalent Rare Earths

Effects of Zr on the Precursor Architecture and High-Temperature Nanostructure Evolution of Sioc Polymer-Derived Ceramics

Promotional Effect Of Zr On Thermal Stability Of Cetiox Monolith Catalyst For Selective Catalytic Reduction Of Nox With Ammonia

The Effect of Rare Earth Modification on Ceria–zirconia Solid Solution and Its Application in Pd-only Three-Way Catalyst

Influence of B-site substituent Ce on thermophysical, oxygen diffusion, and mechanical properties of La2Zr2O7

Effect of thermal treatment at high temperature on phase stability and transformation of Yb2O3 and Y2O3 co-doped ZrO2 ceramics

Improved thermal properties and CMAS corrosion resistance of high-entropy RE zirconates by tuning fluorite-pyrochlore structure