The controlled engineering of surface oxygen defects on Bi2Zr2O7 compounds for catalytic soot combustion by adjusting the preparation methods.
Xiang Wang,Ping Wang,Shijing Zhang,Zekai Xu,Junwei Xu,Yuting Li,Jiating Shen,Xianglan Xu,Xiuzhong Fang,Xiaohui Feng
DOI: https://doi.org/10.1039/d3cp04104b
2023-12-13
Abstract:The quantity of surface oxygen vacancies/defects is critical to promote the reactivity of metal oxide catalysts. Therefore, for the controlled engineering of Bi2Zr2O7 with rich surface defects for soot combustion, four different methods have been adopted. Bi2Zr2O7 compounds with a defective fluorite phase but with varied surface vacancy concentrations have been successfully synthesized by various methods. The best catalyst (Bi2Zr2O7-CP) was fabricated by a facile co-precipitation method. Both O2- and O22- were the active surface sites whose number positively correlated to the number of surface oxygen vacancies and determined the activity. Moreover, a sample with more surface vacancies usually had weaker Zr-O bonds, which could be the intrinsic factor to enhance the activity. In addition, a novel and simple method has been developed to accurately titrate the absolute amount of soot reactive oxygen sites and calculate the TOF values. In conclusion, by optimizing the preparation methods, Bi2Zr2O7 catalysts with rich surface defects can be tuned, which may help in designing more applicable soot oxidation catalysts.
Chemistry,Engineering,Medicine,Materials Science