Abstract:Nanometric CeO2-supported cobalt oxide materials with variable Co/Ce atomic ratios were prepared by the method of ultrasonic-assisted incipient-wetness impregnation. The catalytic behaviors of a series of CoOx/nmCeO2 catalysts have been studied for soot combustion. XRD, XPS, Raman, UV–vis DRS and FT-IR spectroscopy characterization results indicated that CoO or cobalt–cerium solid solutions were formed in the samples with the low Co loading amount, while Co3O4 was formed in the samples with high Co loading amount. CoOx/nmCeO2 catalysts can further promote soot combustion in contrast to nanometric CeO2. This improvement is related to the increase in the redox properties of the catalysts brought about by loading cobalt oxide on nanometric CeO2. The TPR experiment results under hydrogen atmosphere indicated that the presence of Co decreases the reduction temperature of catalyst from 555°C (nanometric CeO2) to 286°C (Co20/nmCeO2). On the other hand, attributing to nanoparticle effect and NO2 formation, Com/nmCeO2 oxide catalysts prepared in this study have very high activity for soot combustion. The best catalytic activity was obtained over Co20/nmCeO2 catalyst that T10, T50, T90 were 286°C, 368°C, 418°C, respectively, and SCO2m was 98.8%. Compared with the blank case (i.e., without catalyst) for soot combustion, T50 decreased by more than 200°C and SCO2m increased by 40% point. And this catalytic activity for the combustion of soot particle is as good as supported Pt catalysts, which is the best catalyst system so far reported for soot combustion under loose contact conditions. This temperature of soot combustion can ensure immediate activation of the catalyst on the filter under the conditions of diesel engine emissions.

Calcination temperature effect on CeO2 catalytic activity for soot oxidation: A combined experimental and theoretical approach.

Soot Combustion Performance and H2-TPR Study on Ceria-Based Mixed Oxides

Preparation, Characterization and Catalytic Activity Studies of CeO2–K Diesel Soot Oxidation Catalysts Loaded on Porous Al2O3 Substrate Using Water-Immiscible Solvent

Design Structure for Cepr Mixed Oxide Catalysts in Soot Combustion

A Comparative Study on Ce–Pr and Ce–Mn Mixed Oxide Catalysts Toward Soot Catalytic Combustion

Surface Adsorbed and Lattice Oxygen Activated by the CeO 2 /Co 3 O 4 Interface for Enhancive Catalytic Soot Combustion: Experimental and Theoretical Investigations

The effects of potassium halides on catalytic activities of CeO2–K based catalysts for diesel soot oxidation

Soot Oxidation over Ceo2 and Ag/Ceo2: Factors Determining the Catalyst Activity and Stability During Reaction

Enhanced Soot Oxidation Activity of a CuO-Doped CeO2 Catalyst via Acid Etching

Effects of a Catalyst on the Nanostructure and Reactivity of Soot under an Oxygen Atmosphere

Thermal Stability of MnO X – CeO 2 Mixed Oxide for Soot Combustion : Influence of Al 2 O 3 , TiO 2 , and ZrO 2 Carriers

Effects of Zr substitution on soot combustion over cubic fluorite-structured nanoceria: Soot-ceria contact and interfacial oxygen evolution

The Effect of Calcination Temperature on the Structure and Activity of TiO2/SiO2 Composite Catalysts Derived from Titanium Sulfate and Fly Ash Acid Sludge

The Highly Active Catalysts of Nanometric CeO2-supported Cobalt Oxides for Soot Combustion

The Catalytic Activity of CuO–CeO2 Mixed Oxides for Diesel Soot Oxidation with a NO/O2 Mixture

An Exploration of Soot Oxidation over CeO2-ZrO2 Nanocubes: Do More Surface Oxygen Vacancies Benefit the Reaction?

Effects of high-temperature CeO 2 calcination on the activity of Pt/CeO 2 catalysts for oxidation of unburned hydrocarbon fuels

Cerium Doping Effect in 3DOM Perovskite-Type La2−xCexCoNiO6 Catalysts for Boosting Soot Oxidation

Selective Oxidation of Soot over Cu Doped Ceria/ceria–zirconia Catalysts

Insight into high-performance of La–Ce–MnOx oxides with different calcination temperatures for diesel soot combustion

Soot combustion over Ag catalysts supported on shape-controlled CeO2