Nature of Active Sites on Cu–CeO 2 Catalysts Activated by High-Temperature Thermal Aging
Beibei Wang,Hui Zhang,Wei Xu,Xiaobao Li,Wei Wang,Lunjia Zhang,Yimin Li,Zheng Peng,Fan Yang,Zhi Liu
DOI: https://doi.org/10.1021/acscatal.0c03188
IF: 12.9
2020-09-28
ACS Catalysis
Abstract:Cu clusters supported on CeO<sub>2</sub> nanorods (NRs) were found to exhibit significantly enhanced activity and thermal/hydrothermal durability for low-temperature CO oxidation when the catalyst was calcined at 800 °C in air prior to the catalytic measurements. The effect of calcination temperature and Cu loading on Cu-CeO<sub>2</sub> catalysts was studied by the combination of powder X-ray diffraction (PXRD), Raman spectroscopy, H<sub>2</sub>-temperature program reduction (H<sub>2</sub>-TPR), ambient-pressure X-ray photoelectron spectroscopy (APXPS), synchrotron radiation photoelectron spectroscopy (SRPES), and X-ray absorption spectroscopy (XAS). Cu atoms were found to incorporate into the ceria lattice in air at below 500 °C, leading to the formation of a bulk Cu<i><sub>y</sub></i>Ce<sub>1–<i>y</i></sub>O<sub>2–<i>x</i></sub> solid solution. As the calcination temperature was raised to 800 °C, the solubility of Cu ions in bulk ceria was reduced sharply. Surface segregation of Cu atoms led to the formation of CuO<i><sub>x</sub></i> and a surface Cu-doped ceria thin layer, resulting in a much enhanced activity for CO oxidation. Moreover, the activities of calcined Cu-CeO<sub>2</sub> catalysts did not increase with the Cu loading but exhibited an optimal activity at ∼2 wt % of Cu loading, where segregated CuO<i><sub>x</sub></i> species gave an average size in the sub-nanometer (sub-nm) range. Larger CuO<i><sub>x</sub></i> nanoparticles (NPs) on the Cu-doped ceria thin layer exhibited a lower activity toward CO oxidation. We believe the enhanced catalytic properties of the thermally aged Cu-CeO<sub>2</sub> catalysts are attributed to the formation of an interface between sub-nm CuO<i><sub>x</sub></i> and the Cu-doped ceria thin layer. Our study thus sheds light on the nature of most active sites on Cu/CeO<sub>2</sub> catalysts and facilitates the rational design of ceria-supported metal catalysts for oxidation reactions.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acscatal.0c03188?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acscatal.0c03188</a>.Details of the XRD patterns, XAS spectra, light-off tests, Raman spectra, XPS spectra, TEM images, O<sub>2</sub>-TPO profiles, and so on (<a class="ext-link" href="/doi/suppl/10.1021/acscatal.0c03188/suppl_file/cs0c03188_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, physical