Abstract:Nanoparticles of CexZr1−xO2 (x=0.75, 0.62) were prepared by the oxidation-coprecipitation method using H2O2 as an oxidant, and characterized by N2 adsorption, XRD and H2-TPR. CexZr1−xO2 prepared had single fluorite cubic structure, good thermal stability and reduction property. With the increasing of Ce/Zr ratio, the surface area of CexZr1−xO2 increased, but thermal stability of CexZr1−xO2 decreased. The surface area of Ce0.62Zr0.38O2 was 41.2m2/g after calcination in air at 900°C for 6h. TPR results showed the formation of solid solution promoted the reduction of CeO2, and the reduction properties of CexZr1−xO2 were enhanced by the cycle of TPR-reoxidation. The Pd-only three-way catalysts (TWC) were prepared by the impregnation method, in which Ce0.75Zr0.25O2 was used as the active washcoat and Pd loading was 0.7g/L. In the test of Air/Fuel, the conversion of C3H8 was close to 100% and NO was completely converted at λ<1.025. The high conversion of C3H8 was induced by the steam reform and dissociation adsorption reaction of C3H8. Pd-only catalyst using Ce0.75Zr0.25O2 as active washcoat showed high light off activity, the reaction temperatures (T50) of 50% conversion of CO, C3H8 and NO were 180, 200 and 205°C, respectively. However, the conversions of C3H8 and NO showed oscillation with continuously increasing the reaction temperature. The presence of La2O3 in washcoat decreased the light off activity and suppressed the oscillation of C3H8 and NO conversion. After being aged at 900°C for 4h, the operation windows of catalysts shifted slightly to rich burn. The presence of La2O3 in active washcoat can enhance the thermal stability of catalyst significantly.

Effect of Preparation Methods on the Structure and Redox Behavior of Platinum–ceria–zirconia Catalysts

Effect of Ce/Zr Atomic Ratio on the TWC Properties of PdO/CexZr1-xO2(x=0-1.0) Catalysts

Influence of the Oxidative/Reductive Treatments on the Activity of Pt/Ce0.67zr0.33o2 Catalyst

Influence of Ceria-Zirconia Solid Solution on Performance of Noble Metal Monolithic Oxidation Catalyst

In-situ Formed Stable Pt Nanoclusters on Ceria-Zirconia Solid Solutions Induced by Hydrothermal Aging for Efficient Low-Temperature CO Oxidation

Catalytic Activity and Characterization of Oxygen Mobility on Pt/Ce0.75Zr0.25O2 Catalyst by Isotopic Exchange with 18O

Effect of Preparation Method on the Surface and Redox Properties of Ce0.67zr0.33o2 Mixed Oxides

Preparation of CexZr1−xO2 (x = 0.75, 0.62) Solid Solution and Its Application in Pd-only Three-Way Catalysts

Preparation of ceria-zirconia by modified coprecipitation method and its supported Pd-only three-way catalyst

The preparation of Pd/CeO2–ZrO2–Al2O3 catalyst with superior structural stability: effect of zirconia incorporation method

Effect of Zirconium Precursor on Performance of Pd/Ce0.45Zr0.45La0.1O1.95 Three-Way Catalyst

A Novel Insight into the Preparation Method of Pd/Ce0.75Zr0.25O2-Al2O3 over High-Stability Close Coupled Catalysts

Improving the catalytic activity and thermal stability of Pt-supported catalyst via modulating Ce/Zr molar ratio

The Effect of Rare Earth Modification on Ceria–zirconia Solid Solution and Its Application in Pd-only Three-Way Catalyst

A Study of Novel Composite Mesoporous Zirconia Catalyst Materials

Preparation of Cex Zr1-x-AI mixed oxides and investigation of the palladium-only three-way catalytic performance

Preparation of Ceria-zirconia Mixed Oxides with Improved Thermal Stability for Three-way Catalysts by a Modified Co-precipitation Method

Modification of Pd–CeO2 Catalyst by Different Treatments: Effect on the Structure and CO Oxidation Activity

Effects of Platinum or Palladium on Structure and Properties of Cr/ZrO2 Catalyst

Preparation, Characterization and Origin of Highly Active and Thermally Stable Pd-Ce0.8zr0.2o2 Catalysts Via Sol-Evaporation Induced Self-Assembly Method

Preparation of CexZr1-xO2 with Combined Composition for Improved Pd-only Three-way Catalyst