Abstract:For the first time, a nanosheet-state CoMnx mixed oxide with multifarious active regions was synthesized by oxidation-etching assembly of metal organic framework (MOF) precursor and applied for catalytic combustion of toluene at low temperatures. The obtained optimum catalyst denoted as CoMn6 showed excellent performance, which achieved 90% conversion of 1,000 ppm toluene under a weight hourly space velocity (WHSV) of 60,000 mL/(g·h) at 219 °C. While, it also exhibited long-term stability with strong water resistance property. The characterizations of physicochemical properties indicated that the oxidation-etching assembly process built an abundant mesoporous structure in the CoMnx catalyst, which greatly increased the specific surface area (SSA). Especially, potassium permanganate as oxidant and manganese source led to uniform dispersion and assembling of cobalt atoms, which caused the generation of low-crystallinity CoMnx mixed oxide with abundant dislocations, vacancies, phase interfaces and amorphous structures, resulting in excellent low-temperature reducibility, outstanding lattice oxygen mobility and abundant active species such as Mn 3+ , Co 3+ and adsorbed oxygen species. Density functional theory (DFT) calculations demonstrated that gaseous oxygen with the longer bond length (1.406 Å) and stronger adsorption energy (−4.443 eV) could be adsorbed and activated well on the MnCo 2 O 4.5 (3 1 1) plane, which is beneficial for the toluene oxidation. In situ diffuse reflectance infrared spectroscopy (DRIFTS) technique was applied to track the intermediates of toluene combustion under different atmospheres, which further deduced the contributions of different active regions and oxidation mechanism over the CoMnx catalyst. The present facile strategy of oxidation-etching assembly of the MOF precursor for the creating of novel catalyst with high performance could be applied in a wide variety of materials besides VOC combustion catalysts.

Toluene combustion over Co3O4-CNTs/PSSF catalysts and investigation of the effects of acid treatment on catalytic activity

Boosting Toluene Combustion in Pt-Co3O4 Catalysts by Directional Tuning Strong Metal-Support Interactions Through Metal-Organic Template Pyrolysis

Catalytic Combustion of VOCs on Pt/CuMnCe and Pt/CeY Honeycomb Monolithic Catalysts

Promote the Efficient Co-Combustion of Toluene & CO in Pt/CeO2 Catalyst: Orientally Adjusting the Oxidized SMSI to Optimize Acid Site and Oxygen Vacancy

Hierarchical laminated Al2O3 in-situ integrated with high-dispersed Co3O4 for improved toluene catalytic combustion

Novel metallic electrically heated monolithic catalysts towards VOC combustion

Preparation of Nickel-Foam-supported Pd/NiO Monolithic Catalyst and Construction of Novel Electric Heating Reactor for Catalytic Combustion of VOCs

Enhancing Oxygen Activation Ability by Composite Interface Construction over a 2D Co3O4-Based Monolithic Catalyst for Toluene Oxidation

Enhanced Catalytic Combustion Performance of Toluene over a Novel Co–CeO x Monolith Catalyst

Non-oxide supported Pt-metal-group catalysts for efficiently CO and toluene co-oxidation: Difference in water resistance and degradation intermediates

Controllable Synthesis of Pd/CuxCo3-xOn Interfaces for Highly Efficient Catalytic Combustion of Toluene

Study on the combustion of toluene by acid etching assisted ultrasonic supported low content Pt catalyst

The Highly Active Catalysts of Nanometric CeO2-supported Cobalt Oxides for Soot Combustion

Nanosheet-state cobalt-manganese oxide with multifarious active regions derived from oxidation-etching of metal organic framework precursor for catalytic combustion of toluene

Engineering Co3O4@3DOM LaCoO3 multistage-pore nanoreactor with superior SO2 resistance for toluene catalytic combustion

Pd-Co Based Spinel Oxides Derived from Pd Nanoparticles Immobilized on Layered Double Hydroxides for Toluene Combustion

Great activity enhancement of Co3O4/γ-Al2O3 catalyst for propane combustion by structural modulation

Effects of support for cobalt catalysts in catalytic oxidation of toluene

Engineering Cobalt Oxide with Coexisting Cobalt Defects and Oxygen Vacancies for Enhanced Catalytic Oxidation of Toluene

Anionic defects engineering of Co3O4 catalyst for toluene oxidation

Catalytic oxidation of VOCs over 3D@2D Pd/CoMn2O4 nanosheets supported on hollow Al2O3 microspheres