Abstract:<p>In this study, the microstructure evolution and mechanical anisotropy of the extruded Mg-2Zn-0.4Mn-0.4Ce alloy tube during tensile loading along the extrusion direction (ED), 45° towards extrusion direction (45°ED) and transverse direction (TD) were investigated, respectively. The results showed that the initial extruded alloy tube had an obvious {0001} basal fiber texture with the symmetrical pole position deviating about 20° from the RD to ED, which resulted in mechanical anisotropy of the tensile yield stress (TYS) when tensile loading along the ED, 45°ED and TD. The deformation behavior of the alloy tube consisted of three stages. In the yield process, the deformation was dominated by prismatic<a>slip under tensile loading along the ED, while the deformation was dominated by basal<a>slip, next were prismatic<a>slip and pyramidal<c+a>slip under tensile loading both along the 45°ED and TD. In the initial stage after yielding, some extension twin (ETW) formed when tensile loading along the three direction, and the deformations were still dominated by the previous slip systems. In the later part of the deformation, the activation of prismatic<a>slip and the nucleation and expansion of ETW gradually reached saturation under tensile loading along the ED. The dominated prismatic<a>slip was gradually replaced by pyramidal<c+a>slip, and accompanied with a small content of contraction twin (CTW) and double twin (DTW), thus forming a typical texture of [0001]⊥ED. For the deformation both along the 45°ED and TD, dominated prismatic<a>slip and subdominant pyramidal<c+a>slip gradually became the main deformation mode after the saturation of basal<a>slip and ETW, and a small content of CTW and DTW also formed, thus forming the texture of [0001]∥ED-RD plane.</a></c+a></a></c+a></a></a></c+a></a></a></a></p>

Grain size and texture analysis of aluminum multi-pipe extrusion tube by electron backscattered diffraction technique

Microstructure Development and Texture Evolution of Aluminum Multi-Port Extrusion Tube During the Porthole Die Extrusion

Analysis of Surface Orange Peel of Automotive Aluminum Alloy Pipe Using Electron Backscatter Diffraction (Ebsd)

An Electron Back-Scattered Diffraction Study on the Microstructure Evolution of AZ31 Mg Alloy During Equal Channel Angular Extrusion

Microstructural and texture evolution investigation of laser melting deposited TA15 alloy at 500?C using in-situ EBSD tensile test

The microstructure evolution and mechanical anisotropy of extruded Mg-2Zn-0.4Ce-0.4Mn alloy tube during tension in different directions

Ebsp Investigation of Microstructure and Texture Evolution During Equal Channel Angular Pressing of Aluminium

Through-Thickness Texture Gradient in Aa 7055 Aluminum Alloy

In-situ EBSD Observation of Texture Evolution and Lattice Rotation Behavior in Shear Deformation of Thin-Walled Aluminum Alloy Tubes

The effect of texture on the mechanical properties of AZ31 MG alloy by equal channel angular extrusion

Quantitative analysis of orange peel during tension of 6063 alloy spun tubes

Microstructure and Texture Evolutions of Aa1050 Aluminum Alloy Cold Rolled to High Strains

In-situ EBSD analysis of microstructural evolution and damage behavior of Mg-Al-Ca-Mn alloys with different extrusion ratios

Microstructure Evolution of AZ31 Alloy under Compression by In-Situ EBSD

Influence of Extrusion Parameters on Grain Size and Texture Distributions of AZ31 Alloy

Microhardness Distribution and Microstructural Evolution in Pure Aluminum Subjected to Severe Plastic Deformation: Elliptical Cross-Sectioned Spiral Equal-Channel Extrusion (ECSEE)

3D Ebsd Characterization of Deformation Structures in Commercial Purity Aluminum

Analysis of Deformation Textures and Microstructure in ECAE Processed Copper Single Crystals Via Route C

Microstructure and Texture Evolution of Particle-Containing Aa3104 Alloy Cold Rolled to Large Strains

Quasi-in-situ Observing the Rare Earth Texture Evolution in an Extruded Mg-Zn-Gd Alloy with Bimodal Microstructure

Recrystallization behavior and texture evolution on extrusion connection process of Mg/Al alloys thickness-oriented bonding sheet