Abstract:In this study, the surface of (Ti-6Al-4V)TC4 alloy was modified via laser cladding. The elemental composition of the coating was (TiAl)95−xCu5Nix, with Ni as the variable (where x = 0, 3, 6, and 9 at.%). Multi-principal alloy coatings were successfully prepared, and their constituent phases, microstructures, and chemical compositions were thoroughly investigated. The hardness and wear resistance of the coatings were analyzed, and the compositions and interfacial characteristics of the different phases were examined via transmission electron microscopy. The analysis revealed that Ni formed a solid solution and a eutectic structure in the Ti(Al, Cu)2 phase. These findings provide valuable insights into the coating properties. Moreover, reciprocal dry sliding friction experiments were conducted to investigate the wear mechanism. The results revealed a significant increase in wear resistance owing to the formation of a Ni solid solution and changes in the coating structure. Additionally, tensile tests demonstrated that the tensile strength of the coatings initially increased and then decreased with varying Ni content. By combining these results with various analyses, we determined that the coating exhibited optimal properties at a Ni content of 6 at.%. Overall, this study comprehensively investigated the microstructure and phase transition behavior of these coatings through various analytical techniques. These findings provide valuable guidance for further optimizing both the preparation process and the performance of the coatings. The coatings exhibit excellent wear resistance and could inspire the design of more advanced protective surfaces.

Microstructure and properties of AlTiN-Cu coating

Microstructure and Mechanical Properties of TiAlCrN and TiAlCrN/CrN Composite Coatings by Arc Ion Plating

Microstructure and Properties of the AlCrSi(O)N Tool Coatings by Arc Ion Plating

Microstructure and mechanical properties of nanomultilayered AlTiN/Cu coatings prepared by a hybrid system of AIP and PDCMS

Properties and Performance of TiAlSiN and AlCrN Monolayer and Multilayer Coatings for Turning Ti-6Al-4V

Effects of Ultrasonic Shot Peening and Multi-arc Ion Plating on Microstructure and Properties of TiAlN-Coated Cemented Carbide Materials

Investigations on microstructure, mechanical and tribological properties of TiN coatings deposited on three different tool materials

Effect of Arc Current on the Microstructure of AlTiN-Coated Tools and Milling of 304 Stainless Steel

Effect of Cu doping on the microstructure and mechanical properties of AlTiVN-Cu nanocomposite coatings

Mechanical, oxidation, and cutting properties of AlCrN/AlTiSiN nano-multilayer coatings

Effects of C content on the microstructure, mechanical and tribological properties of TiAlSiCN coatings

Study on the growth and wear behavior of the TiAlN-based composite coating deposited on TiCN-based cermets with different binder phase

Tribological Properties and Preparation of (Ti,Al)N Coatings on High Speed Steel Substrate

Microstructures and Mechanical Properties of (Ti,Cr)N Composite Coatings Grown by Arc Ion Plating

Properties of TiAlCrN coatings prepared by vacuum cathodic arc ion plating

Fabrication and Characterization of In-Situ Duplex Plasma-Treated Nanocrystalline Ti/AlTiN Coatings

The Effect of Al Element on the Microstructure of Ti1-xAlxN Coating

Microstructural and Performance Analysis of (TiAl)95−xCu5Nix Coatings Prepared via Laser Surface Cladding on Ti–6Al–4V Substrates

Microstructure and Properties of TiAlN Coating Prepared by Magnetron Sputtering on Titanium Alloy

Microstructure, Tribological and Cutting Performance of Ti-DLC/α-C:H Multilayer Film on Cemented Carbide

Influence of film structure on the microstructure and properties of TiAlN coatings on Al-Si alloys