Effect of Arc Current on the Microstructure of AlTiN-Coated Tools and Milling of 304 Stainless Steel

Simin Zou,Zixiang Luo,Yingxin Li,Liang Yuan,Yu Tang,Jialin Zhou,Huizhong Li

DOI: https://doi.org/10.3390/coatings14060704

IF: 3.236

2024-06-05

Coatings

Abstract:304 stainless steel demonstrates a low thermal conductivity and work hardening characteristics, resulting in its processing, and will adhere to the tip of the tool; as well as the phenomenon of chipping, shortening the life of the tool. AlTiN coatings are representative of coatings applied to carbide tools. In this paper, AlTiN coatings with different arc current processes were deposited on carbide milling inserts using arc ion plating. The microstructure, mechanical properties, and milling properties of the coatings were investigated by using the SEM, EDS, XRD, scratch meter, friction and wear meter, and vertical machining center. The findings revealed that all coatings displayed columnar crystal growth, free from cracks and voids. With an increasing arc current, there was a notable increase in surface droplets, pits, and coating thickness. The coating deposited at a 140 A arc current showed a pronounced (200) orientation preference. The adhesion force peaked at 56.0 N with a subsequent decline, and the friction coefficient hit its lowest point of 0.429 at 140 A, contrasting with its highest value of 0.55 at 160 A. After 39 min of dry milling, the tool with a 140 A AlTiN coating exhibited minimal wear of 0.196 mm, just below the 0.2 mm failure threshold, indicating superior performance at this arc current setting.

materials science, multidisciplinary, coatings & films,physics, applied

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is the problems of tool adhesion, chipping and shortened tool life of 304 stainless steel during processing due to its low thermal conductivity and work - hardening characteristics. Specifically, the author explores the optimal arc current parameters by studying the influence of AlTiN coatings deposited under different arc current conditions on the microstructure, mechanical properties and milling performance of tools, so as to improve the processing efficiency and surface quality of 304 stainless steel. It is mentioned in the paper that during the processing of 304 stainless steel, element inter - diffusion is likely to occur, resulting in tool adhesion. This will not only reduce the sharpness of the tool and slow down the processing speed, but also make the surface roughness of the workpiece not up to standard. In addition, the low plasticity of 304 stainless steel will also cause tool chipping during processing, further shortening the tool life and reducing the processing efficiency.

To deal with these problems, the researchers adopted the method of depositing AlTiN coatings on cemented carbide tools. Using arc ion plating technology (AIP), they studied the microstructure, mechanical properties and milling performance of AlTiN coatings deposited under different arc currents (120 A, 140 A, 160 A, 180 A). The experimental results show that as the arc current increases, the number of droplets on the coating surface increases and the coating thickness increases. Moreover, the coating deposited under an arc current of 140 A shows the best (200) crystal plane orientation preference, with the highest adhesion (56.0 N) and the lowest friction coefficient (0.429). After 39 minutes of dry milling, the wear amount of the AlTiN - coated tool deposited under an arc current of 140 A is only 0.196 mm, close to but not reaching the failure threshold of 0.2 mm, showing superior performance under this arc current setting.

In conclusion, this paper aims to improve the processing performance of 304 stainless steel, extend the tool life and increase the processing efficiency by optimizing the deposition process parameters of AlTiN coatings, especially the arc current.