Microstructure and Mechanical Properties of TiAlCrN and TiAlCrN/CrN Composite Coatings by Arc Ion Plating

陈灵,曾德长,邱万奇,董小虹,黎炳雄,黄拿灿

DOI: https://doi.org/10.3321/j.issn:1004-0609.2009.09.012

2009-01-01

The Chinese Journal of Nonferrous Metals

Abstract:TiAlCrN and TiAlCrN/CrN composite coatings were prepared on the substrate of high speed steel(M2).The substrates were initially plasma nitrided(PN) to create a diffusion layer, and the arc ion plating was applied to deposit TiAlCrN and TiAlCrN/CrN multilayers.The microstructure of the deposited coatings was characterized by electron probe microanalysis(EPMA), scanning electron microscopy(SEM) and X-ray diffractometry(XRD).The results show that TiAlCrN and TiAlCrN/CrN coatings exhibit weak(111) and(200) orientations, respectively, though both of them have a crystal structure of FCC.The composition and microstructure of TiAlCrN coating are homogeneous and uniform.Compared with TiAlCrN coating, TiAlCrN/CrN multilayers tested by nanoindentation and microscratch with a periodic structure consisting of alternating TiAlCrN layer with thick of 400 nm and CrN layer with thick of 200 nm exhibit higher hardness of about 3 450 HV and higher adhesion strength of more than 100 N.