Abstract:The work aims to obtain TiB2-Ni(Al) composite powder through in-situ synthetic technology. Ni(Al)-based com-posite powder reinforced by TiB2 ceramic phase with different volume contents was prepared by mechanical alloying method under different ball milling time. The molar ratio of Ni and Al was 1:1. The microstructure and phase of ball-milled powder were analyzed with scanning electron microscopy (SEM) and X-ray diffraction (XRD) respectively. The influence of various ball mil-ling time on the phase evolution of TiB2-Ni(Al) composite powder prepared, microstructure and interfacial bonding between particles was studied. In the process of ball milling, with the milling time prolonging, the plastic deformation between Ni/Al was conducive to atom diffusion and the size of TiB2 ceramic phase particle became smaller and smaller. When the ball milling time increased to a certain extent, the Al powder particles of good ductility would be flattened and its surface area became larger. In such case, the broken Ni powder particles were embedded into Al powder particles to finally form Ni(Al) solid solution. Mean-while, according to the analysis of XRD, with the ball milling prolonging, Al peak in TiB2-Ni(Al) composite powder was gradu- ally decreased, which revealed that Al constantly diffused into Ni to form a certain amount of Ni(Al) solid solution. Ni(Al) solid solution can be successfully in-situ synthesized by mechanical ball milling technology after a certain milling time, so it is re-vealed that the inter-diffusion between Ni and Al is in favor of forming Ni(Al) solid solution.

Microstructure of TiB2-Ni(Al) Composite Powder Prepared by Mechanical Alloying

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

Preparation of ti-al based nanophase composite powder by mechanical alloying

Mechanical Alloying and Spark Plasma Sintering of Ni-Al-Ti-B Powders for Fabricating Nanocrystailine (Tib+tib2)/ni-3(Al, Ti) Composite

Synthesis of NiAl(Cr,Nb) Powder by Mechanical Alloying

Microstructure And Characteristics Of Ti-Nb-Sn-Ha Composite Powder Fabricated By Mechanical Alloying

Mechanical alloying of Ti/Al binary powders

Preparation and Characterization of TiB2/Al3Ti/Al2O3 Composite Nano-powder

Microstructure evolution of TiAl composite powder during low temperature high-energy milling

Microstructure evolution of Ti/BN powder blend during ball milling and heat treatment

Deposition of NiAl/Al3Ni2(CrB2) Coatings from Ni, Al and CrB2 Powders Using Mechanical Synthesis in Planetary Ball Mill

Preparation of Cbnp/Nicral Nanostructured Composite Powders by A Step-Fashion Mechanical Alloying Process

SYNTHESIS OF NANOSTRUCTURED GAMMA-TiAl BASED POWDERS AND BULK ALLOYS USING HIGH ENERGY MECHANICAL MILLING AND HIP

Evolution of microstructures of Ti/AI binary powders during mechanical alloying process

Preparation of TiAl-based alloys by mechanical milling and reactive sintering

TiB2/TiC nano-composite powder fabricated via high energy milling

Preparation, Microstructures and Mechanical Properties of In-Situ TiB2/Al Composites by Mechanical Stirring and Subsequent Ultrasonic Treatment

Effect of Mechanical Activation on the Morphology and Microstructure of Ni-Al-Ti-B Composite Powders

Microstructures and Solidification Behavior of Rapidly Solidified TiB2 Reinforced Al-Si Composite Powders

Microstructure and formation mechanism of Ni-Al intermetallic compounds fabricated by reaction synthesis

Investigation on nanocrystalline TiAl based powders prepared by double-steps ball milling