Abstract:A 6061 alloy honeycomb with 54 μm thick Al2O3coatings was prepared by the hard anodic oxidation technique,and then the thermal residual stresses were measured by X-ray diffraction (XRD) method.The section morphology of the coating was characterized by scanning electron microscopy and optical microscope.The influence of thermal loads on the residual stress in both the coating and substrate was investigated via both experiment and theoretical methods.The residual stresses obtained from the XRD technology show good agreement with the estimated results from the theoretical model.The results show that the coating is composed of γ-Al2O3.In the range of 400 ℃ to 500 ℃,as the temperature increases,the crack number in the coating increases,but the interface between the coating and the substrate is still perfect.As the temperature reaches 600 ℃,a large number of cracks are found near the interface,and delamination failure occurs at the same time.

Analysis of residual stresses and failure of aluminum honeycomb with Al2O3 coating under thermal loads