Cause Analysis and Precaution of Striation Defects of St12 Cold Rolled Coil

He DING,Guifang ZHANG,Chunlei YANG,Jinzhu LI

DOI: https://doi.org/10.14158/j.cnki.1001-3814.2017.01.071

2017-01-01

Abstract:Striation defects of St12 cold rolled coil were analyzed. The main reasons for the defects were obtained. The results show that: there are obvious transverse cracks in the cast specimens, and there are triangle area cracks and needle-like bubbles during the low-magnification analysis, but the level of needle bubble is lower, and the bubbles can not be observed by the naked eye. From the macro-morphology of defects and metallographic analysis of view, edge tongue shape defect is formed by casting slab corner crack rolling; from the view of the metallographic and the electron microscope analysis of the cold rolled plate and the hot rolled plate,in both /either of which the slag chemical elements K, Na, Ca appear. The closed defect of the sub surface layer of some samples is caused by the rolling slag. It is suggested that the liquid level and pulling speed should be further stabilized, argon flow rate shold be controlled and the slag and gas should be reduled in the steel making continuous casting.