Effect of adding trace metal ions and metal oxide on corrosion property of anode aluminum foil and mechanism analysis

Xian SUN,Jinke CHENG,Rengui XIAO,Kaifang ZHU,Hui LI

DOI: https://doi.org/10.14106/j.cnki.1001-2028.2018.02.007

2018-01-01

Abstract:For studying the influence factors and action mechanism of adding trace metal ions in HCl-H2SO4DC etching system, the reduction rate and the mass loss rate of aluminum foil were analyzed. The morphology of the corrosion aluminum foil was tested by OM and SEM. The results show that, because of the balance of occupying active site effect, galvanic cell effect and competition effect, the reduction rate of aluminum foil decreased first, increased later, then decreased again, while the variation of the weight-loss rate is complex relatively with increasing of metal ions or oxide concentration. A corrosion inhibition is occured, the most about 59.7% reduction rate and 13.5% weight-loss rate are decreased after adding low-concentration metal ions. The denser tunnels, the less useless etching of Cl–, the higher specific surface area and specific capacitance are presented. The specific capacitance is enhanced most about 17.1% after adding metal ions or oxide.