Influence of Trace Mg on Corrosion Structure of High Voltage Aluminum Foil

毛卫民,杨宏,余永宁,冯惠平,徐进

DOI: https://doi.org/10.3321/j.issn:1004-0609.2003.05.001

2003-01-01

Abstract:The cube texture and corrosion structure of aluminum anode foil for high voltage electrolytic capacitor containing trace Mg were investigated based on quantitative cube texture analysis and microstructure observation under scanning electron microscope. The effect of Mg content on specific capacity of the foils was also studied. It is deduced that the difference on corrosion structure is related to the content of trace Mg. When Mg content is increased from 0.000 1% to 0.001 4%, Mg will concentrate severely on the surface layer and will lead to the formation of oxide particles containing Mg. The complex oxide particles can result in development of etching tunnel in side directions. The surface corrosion layer will flake off and the specific capacity of the foils at 500 V will be reduced from 7.3×10~(-3) F/m~2 to 4.3×10~(-3) F/m~2, if the frequency of the side development of etching tunnel is high enough.