Abstract:Hexagonal boron nitride (h-BN) h-BN) ceramics have become exceptional materials for heat-resistant components in hypersonic vehicles, owing to their superior thermal stability and excellent dielectric properties. However, their densification during sintering still poses challenges for researchers, and their mechanical properties are rather unsatisfactory. In this study, SrAl2Si2O8 2 Si 2 O 8 (SAS), with low melting point and high strength, was introduced into the h-BN ceramics to facilitate the sintering and reinforce the strength and toughness. Then, BN-SAS ceramic composites were fabricated via hot press sintering using h-BN, SrCO3 , 3 , Al2O3 , 2 O 3 , and SiO2 2 as raw materials, and effects of sintering pressure on their microstructure, mechanical property, and thermal property were investigated. The thermal shock resistance of BN-SAS ceramic composites was evaluated. Results show that phases of as-prepared BN-SAS ceramic composites are h-BN and h-SrAl 2 Si 2 O 8 . With the increase of sintering pressure, the composites' densities increase, and the mechanical properties shew a rising trend followed by a slight decline. At a sintering pressure of 20 MPa, their bending strength and fracture toughness are (138 +/- 4) MPa and (1.84 +/- 0.05) MPam1/2 , 1/2 , respectively. Composites sintered at 10 MPa exhibit a low coefficient of thermal expansion, with an average of 2.96x10-6 -6 K -1 in the temperature range from 200 to 1200 degrees C. The BN-SAS ceramic composites prepared at 20 MPa display higher thermal conductivity from 12.42 to 28.42 Wm-1K-1 -1 K -1 within the temperature range from room temperature to 1000 degrees C. Notably, BN-SAS composites exhibit remarkable thermal shock resistance, with residual bending strength peaking and subsequently declining sharply under a thermal shock temperature difference ranging from 600 to 1400 degrees C. The maximum residual bending strength is recorded at a temperature difference of 800 degrees C, with a residual strength retention rate of 101%. As the thermal shock temperature difference increase, the degree of oxidation on the ceramic surface and cracks due to thermal stress are also increased gradually.

Thermal Shock Resistance of Nano BN-SiC Composites

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Thermal shock resistance of in situ formed SiC–BN composites

Thermal Shock Resistance of Si3N4/h-BN Composites Prepared Via Catalytic Reaction-Bonding Route

Thermal Shock Behavior of Si3N4/BN Fibrous Monolithic Ceramics

Thermal Shock Behavior of Si 3 N 4 /BN Fibrous Monolithic Ceramics.

Thermal Shock Resistance of the Porous Boron Nitride/silicon Oxynitride Ceramic Composites

Effect of Boron Nitride Content on Mechanical、dielectric and Thermal Shock Resistance Properties of Si3N4-BN-MAS Composites

FABRICATION AND THERMAL SHOCK RESISTANCE OF THE MACHINABLE BN/B4C COMPOSITE CERAMICS

Study on Thermal Shock Behavior of SiC/BN Laminated Ceramic Composites

Effect of the BN Content on the Thermal Shock Resistance and Properties of BN/SiO2 Composites Fabricated from Mechanically Alloyed SiBON Powders

Microstructure, mechanical properties and thermal shock behavior of h-BN-SiC ceramic composites prepared by spark plasma sintering

Thermal Shock Resistance Behavior of Machinable Al2O3/BN Nanocomposites

Effect of SiC Content on Mechanical Properties and Thermal Shock Resistance of BN–ZrO2–SiC Composites

Enhanced Strengths and Thermal Shock Resistance of SiC-BN-10 Vol% Cf Composites Through ZrB2 Addition

Microstructural Features and Properties of the Nano-Crystalline SiC/BN(C) Composite Ceramic Prepared from the Mechanically Alloyed SiBCN Powder

Single-cycle thermal shock resistance of ZrB2–SiCnp ceramic composites

High-pressure synthesis of Al<sub>2</sub>O<sub>3</sub>-cBN composites: Effect of thermodynamic condition and cBN volume fraction on their microstructure and properties

Mechanical Properties and Thermal Shock Resistance of SrAl2Si2O8

Microstructure, mechanical properties and thermal shock behavior of h-BN–AlN ceramic composites prepared by combustion synthesis