Effects of Mn precursors on performance of supported Mn/Al2 O3 catalysts for selective catalytic reduction of NO

Xiaowei Lü,Yafeng WAN,Bo LIU,Shizhe ZHANG,Jinjing TANG,Jun DU

DOI: https://doi.org/10.3969/j.issn.1008-1143.2014.12.012

2014-01-01

Abstract:Using manganese acetate,manganese sulfate and the mixture of manganese acetate-manganese sulfate as Mn precursors,respectively,Mn/Al2 O3 catalysts were prepared by the impregnation method. The as-prepared Mn/Al2 O3 catalysts were characterized by BET,XRD,FT-IR,H2-TPR and NH3-TPD. The de-NOx activity and sulfur tolerance properties of Mn/Al2 O3 catalysts were investigated. The results indicated that the crystal and the specific surface area of the catalysts were apparently different due to different Mn precursors. The total acid amount and acid strength of the catalyst surface were enhanced with the addition of manganese sulfate. Compared with the catalysts prepared with manganese acetate and manganese sulfate ,the catalysts prepared with mixture of manganese acetate and manganese sulfate could improve the conversion of NO at( 300-450 )℃,and when SO2 volume fraction in the feed stream was 0. 2%,the activities of the catalyst for De-NOx declined slightly,and its sulfur tolerance properties was the best. Therefore,the catalysts prepared with composite precursor could improve the catalytic activity and the sulfur resistance of the catalyst at high temperature.