Abstract:The structure and catalytic properties of anatase and rutile supported manganese oxide catalysts prepared by impregnation method have been studied by using X-ray diffraction (XRD), laser Raman spectroscopy (LRS), X-ray photoelectron spectroscopy (XPS), H(2) temperature-programmed reduction (H(2)-TPR) and BET surface area measurements combined with activity testing of selective catalytic reduction (SCR) of NO by NH(3). It has been shown that the manganese oxide loadings on the two TiO(2) supports exert great influences on the SCR activity. For the rutile supported manganese oxide catalysts, increasing manganese oxide loading leads to the increase of reducibility of dispersed manganese oxide species and the rate constant k, which reaches a maximum around 9.6 × 10(-6) mol g(Mn)(-1) s(-1) at 0.5 mmol Mn per 100 m(2) TiO(2). When the manganese oxide loading is beyond this value, the existence of amorphous MnO(x) multiple layers will certainly reduce the ratio of manganese oxide species exposed on the surface and the reducibility of dispersed manganese oxide species, resulting in the rapid decrease of rate constant k. The LRS and XPS results have revealed that for the anatase supported manganese oxide catalysts manganese oxide species exist in Mn(+4) as a major species with Mn(+3) species and partially undecomposed Mn-nitrate as the minor species. Under the SCR reaction conditions, Mn(+3) species on anatase are oxidized to Mn(+4) species, inserting in the surface of anatase and promoting the anatase-to-rutile transformation in the surface layers of the anatase support. Since these Mn(4+) cations are actually dispersed on the support with a rutile shell-anatase core structure and its concentration is very near to that of MnO(x)/TiO(2) (R) catalyst, the relation between the rate constant k and the MnO(x) loading on the anatase support is similar to that on the rutile support, and that the rate constant k values for anatase and rutile supported manganese oxide catalysts are very close at the same MnO(x) loading.

Effects of Precursors on the Surface Mn Species and the Activities for NO Reduction over MnOx/TiO2 Catalysts

Effects of precursors on the surface Mn species and SCR activities of MnOX/TiO2 catalysts

Effects of ferric and manganese precursors on catalytic activity of Fe-Mn/TiO2 catalysts for selective reduction of NO with ammonia at low temperature

Insights into the Precursor Effect on the Surface Structure of Γ-Al2o3 and NO + CO Catalytic Performance of CO-pretreated CuO/MnOx/γ-Al2O3 Catalysts.

Effect of MnO(x) Modification on the Activity and Adsorption of CuO/Ce(0.67)Zr(0.33)O(2) Catalyst for NO Reduction.

Effects of Nd-modification on the Activity and SO2 Resistance of MnOx/TiO2 Catalysts for Low-Temperature NH3-SCR

Effects of Precursors for Manganese-Loaded Γ-Al2o3 Catalysts on Plasma-Catalytic Removal of O-Xylene

Low-temperature selective catalytic reduction of NO on MnOx/TiO2 prepared by different methods

Insight into structure defects and catalytic mechanism for NO oxidation over Ce0.6Mn0.4Ox solid solutions catalysts: Effect of manganese precursors

The structure and catalytic activity of anatase and rutile titania supported manganese oxide catalysts for selective catalytic reduction of NO by NH3

Study of the Promotion Effect of Iron on Supported Manganese Catalysts for No Oxidation

Oxidation of Toluene over Mesoporous MnO2/CeO2 Nanosphere Catalysts: Effects of the MnO2 Precursor and the Type of Support

Low-temperature selective catalytic reduction of NO with NH3 over Mn–Ce–Ox/TiO2: a comparison between catalyst preparation methods

Promotional effect of iron oxide on the catalytic properties of Fe–MnOx/TiO2 (anatase) catalysts for the SCR reaction at low temperatures

Mesoporous MnOx-CeO2 composites for NH3-SCR: the effect of preparation methods and a third dopant

Effect of Preferential Exposure of Anatase TiO2 {0 0 1} Facets on the Performance of Mn-Ce/TiO2 Catalysts for Low-Temperature Selective Catalytic Reduction of NOx with NH3

MnOx/TiO2 Composite Nanoxides Synthesized by Deposition-Precipitation Method As a Superior Catalyst for NO Oxidation

Insights over Titanium Modified FeMgOx Catalysts for Selective Catalytic Reduction of NOx with NH3: Influence of Precursors and Crystalline Structures

Origin of the Superior Activity of Surface Doped SmMn2O5 Mullites for NO Oxidation: A First-Principles Based Microkinetic Study

Catalytic oxidation of NO over SmMn2O5 nanostructures derived from different Mn precursors

Investigation and Characterization on MnO_x/TiO_2 for Low-Temperature Selective Catalytic Reduction of NO_x with NH_3