Abstract:Manganese oxides with varied Mn valance states but identical morphologies were synthesized via a facile thermal treatment of γ-MnOOH. Also, their catalytic performance on ozone decomposition was investigated following the order of Mn3O4 < Mn2O3 < MnO2 < MnO2-H-200. In combination with X-ray diffraction (XRD), scanning electron microscopy (SEM), Brunauer–Emmett–Teller (BET), transmission electron microscopy (TEM), H2-temperature-programmed reduction (TPR), O2-temperature-programmed desorption (TPD), and X-ray photoelectron spectroscopy (XPS) characterization, it was deduced that the superior O3 decomposition capacity for MnO2-H-200 was strongly associated with abundant oxygen vacancies on its surface. Among Mn3O4, Mn2O3, and MnO2, the difference in O3 decomposition efficiency was dependent on the divergent nature of oxygen vacancy. Density functional theory (DFT) calculation revealed that Mn3O4 and MnO2 possessed lower formation energy of oxygen vacancy, while MnO2 had the minimum desorption energy of peroxide species (O2*). It was deduced that the promotion of the O3 decomposition capability was attributed to the easier O2* desorption. Insights into the deactivation mechanism for MnO2-H-200 further validated the assumptions. As the reaction proceeded, adsorbed oxygen species accumulated on the catalyst surface, and a portion of them were transformed to lattice oxygen. The consumption of oxygen vacancy led to the deactivation of the catalyst.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.langmuir.0c02841?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.langmuir.0c02841</a>.Catalyst preparation; catalyst characterization; XRD patterns of the as-prepared γ-MnOOH; N2 adsorption and desorption isotherms of different MnOx catalysts; top plane view and the oxygen vacancy sites of the preferentially exposed crystal plane for various MnOx during DFT calculation; FT-IR spectra of MnO2-H-200 and partially deactivate MnO2-H-200 catalysts; ozone conversion over MnO2-H-200 and the regenerated MnO2-H-200; the pore size distribution of different MnOx catalysts calculated by the BJH method (<a class="ext-link" href="/doi/suppl/10.1021/acs.langmuir.0c02841/suppl_file/la0c02841_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Effects of Precursors for Manganese-Loaded Γ-Al2o3 Catalysts on Plasma-Catalytic Removal of O-Xylene

Catalytic performance improvement of VOCs oxidation over MnOx and GdMnO3 composite oxides from spent lithium-ion batteries: Effect of acid treatment

In Situ Fabrication of Highly Active Γ-Mno2/smmno3 Catalyst for Deep Catalytic Oxidation of Gaseous Benzene, Ethylbenzene, Toluene, and O-Xylene.

Investigation of suitable precursors for manganese oxide catalysts in ethyl acetate oxidation

Mn2O3/γ-Al2O3 catalysts synergistic double dielectric barrier discharge (DDBD) degradation of toluene, ethyl-acetate and acetone

Combined Experimental and Theoretical Study of O-Xylene Elimination on Fe–Mn Oxides Catalysts

Investigation on removal of multi-component volatile organic compounds in a two-stage plasma catalytic oxidation system - Comparison of X (X=Cu, Fe, Ce and La) doped Mn2O3 catalysts

The Effects of Mn Loading on the Structure and Ozone Decomposition Activity of MnOx Supported on Activated Carbon

Effects of precursors on the surface Mn species and SCR activities of MnOX/TiO2 catalysts

Catalytic ozonation of dichloromethane at low temperature and even room temperature on Mn-loaded catalysts

To Promote Ozone Catalytic Decomposition by Fabricating Manganese Vacancies in ε-MnO2 Catalyst via Selective Dissolution of Mn-Li Precursors

Degradation of Gas-Phase O-Xylene Via Combined Non-Thermal Plasma and Fe Doped LaMnO3 Catalysts: Byproduct Control.

Effects of Precursors on the Surface Mn Species and the Activities for NO Reduction over MnOx/TiO2 Catalysts

Engineering Mn–O Strength in Manganese Oxide Catalyst to Enhance Propane Catalytic Oxidation

Insights into the Reactive and Deactivation Mechanisms of Manganese Oxides for Ozone Elimination: The Roles of Surface Oxygen Species

Regulating oxygen vacancies and hydroxyl groups of α-MnO2 nanorods for enhancing post-plasma catalytic removal of toluene

Insights into the Precursor Effect on the Surface Structure of Γ-Al2o3 and NO + CO Catalytic Performance of CO-pretreated CuO/MnOx/γ-Al2O3 Catalysts.

Effects Of Precursor And Sulfation On Oms-2 Catalyst For Oxidation Of Ethanol And Acetaldehyde At Low Temperatures

Catalytic Acetone Oxidation over MnOx Catalysts: Regulating Their Crystal Structures and Surface Properties

Boosting the Catalytic Performance of Volatile Organic Compound Oxidation Over Platelike MnO 2 /CoAlO Catalyst by Weakening the Co–O Bond and Accelerating Oxygen Activation

Investigation into enhanced performance of toluene and Hg0 stimulative abatement over Cr-Mn oxides co-modified columnar activated coke