Enhanced Catalytic Oxidation of Chlorobenzene over MnO 2 Grafted In Situ by Rare Earth Oxide: Surface Doping Induces Lattice Oxygen Activation
Lizhong Liu,Ruoyu Liu,Tong Xu,Qiang Zhang,Yubin Tan,Qiaoling Zhang,Jiandong Ding,Yanfeng Tang
DOI: https://doi.org/10.1021/acs.inorgchem.0c02197
IF: 4.6
2020-09-13
Inorganic Chemistry
Abstract:A series of highly active MnO<sub>2</sub>@REO<sub><i>x</i></sub> (RE = Gd, Sm, Ce, and La) catalysts were successfully synthesized via in situ growth on the surface of MnO<sub>2</sub>, wherein the rare earth oxides were planted on the defect sites left by hydrogen peroxide etching of the surface of MnO<sub>2</sub>. Their physicochemical performance was investigated by scanning electron microscopy with energy-dispersive spectroscopy (SEM-EDS), X-ray diffraction (XRD), N<sub>2</sub> adsorption–desorption, X-ray photoelectron spectroscopy (XPS), temperature-programmed reduction with hydrogen (H<sub>2</sub>-TPR), and temperature-programmed desorption of oxygen (O<sub>2</sub>-TPD). The catalytic properties are compared through the catalytic oxidation of chlorobenzene. Among all catalysts, MnO<sub>2</sub>@GdO<sub><i>x</i></sub> showed better mobility of surface lattice oxygen and higher molar ratios of Mn<sup>4+</sup>/Mn<sup>3+</sup> (1.10) and O<sub>ads</sub>/O<sub>latt</sub> (0.45), which promoted the superior low-temperature catalytic activity for chlorobenzene oxidation. The long-term chlorobenzene oxidation test (18 h) at different temperatures and the experiments with a mixture of VOCs showed that the as-prepared catalyst not only possessed a high stability but also was suitable for the efficient and simultaneous removal of multicomponent VOCs (toluene, benzene, acetone, and chlorobenzene). This work also provided an idea for the further development of high-efficiency catalysts for the purification of VOCs from complex atmosphere environment.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.inorgchem.0c02197?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.inorgchem.0c02197</a>.Chemicals and materials, characterization, SEM image of MnO<sub>2</sub>, XPS spectra of La, Ce, Sm, and Gd on the surface of MnO<sub>2</sub>, chlorobenzene oxidation over MnO<sub>2</sub>@GdO<sub><i>x</i></sub> catalysts prepared by using different concentrations of gadolinium nitrate, summary of previous study on the conversion of chlorobenzene over Mn-based oxides, and SEM-EDS elemental mapping images of MnO<sub>2</sub>@GdO<sub><i>x</i></sub> after chlorobenzene oxidation (<a class="ext-link" href="/doi/suppl/10.1021/acs.inorgchem.0c02197/suppl_file/ic0c02197_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, inorganic & nuclear