Abstract:A series of TiO2 supported iron-manganese mixed oxide catalysts were studied for catalytic oxidation of NO to NO2. The oxidation activity was greatly enhanced with the addition of iron, by about 34% at 300 degrees C. Mn0.1Fe0.15/Ti with the molar ration of Mn:Fe = 1:1.5 showed the best oxidation activity. It was also found that the addition of iron oxide increased the resistance to H2O and SO2. The formation of byproduct N2O could generally be disregarded. A combination of various physico-chemical techniques was used to characterize the physical and chemical properties of these catalysts. The surface area did not change very much with the addition of iron. The XRD (X-ray diffraction) and HR-TEM (high-resolution transmission electron microscopy) results suggested that there was an interaction between manganese and iron, leading to the formation of manganese-iron composite oxides, which were in the amorphous phase. The XPS (X-ray photoelectron spectroscopy) and H-2-TPR (temperature-programmed reduction) investigations demonstrated that this composite oxide with an amorphous structure increased the surface active oxygen, facilitated oxygen mobility and enhanced the oxidation-reduction ability over the catalysts, all of which were crucial factors for the increase in NO oxidation activity. The FTIR (Fourier transform infrared spectroscopy) results showed that nitrates worked as intermediates which could be easily decomposed to nitrogen oxides. The introduction of iron into manganese oxides increased the formation of intermediates and reduced the formation of sulfates on the surface of the catalysts.

Study of the Promotion Effect of Iron on Supported Manganese Catalysts for No Oxidation

Manganese-Based Catalysts Supported on Titania for the Oxidation of Nitric Oxide

Enhanced low-temperature NO oxidation by iron-modified MnO2 catalysts

Promotional effect of iron oxide on the catalytic properties of Fe–MnOx/TiO2 (anatase) catalysts for the SCR reaction at low temperatures

Catalytic Oxidation of NO over Fe-Doped MnO2 Catalyst

Assisting Effect of Al2O3 on MnOx for NO Catalytic Oxidation

Promotion effect of tungsten and iron co-addition on the catalytic performance of MnOx/TiO2 for NH3-SCR of NOx

Effect of MnO(x) Modification on the Activity and Adsorption of CuO/Ce(0.67)Zr(0.33)O(2) Catalyst for NO Reduction.

Study on the Effect of Fe Doping on SCR Activity and Reaction Mechanism of Mn–TiO2 Catalysts

Effects of different manganese precursors as promoters on catalytic performance of CuO-MnOx/TiO2 catalysts for NO removal by CO.

Mechanism Study Of No Catalytic Oxidation Over Mnox/Tio2 Catalysts

Catalytic Oxidation of NO over MnOx–CeO2 and MnOx–TiO2 Catalysts

The Synergy Between Manganese Oxide and Iron Oxide in NO Catalytic Removal with MnFeOx/SiO2 Catalyst

Molybdenum-containing oxide catalysts for selective catalytic reduction of NOx with NH3

Promotional Effect of Manganese on Selective Catalytic Reduction of NO by CO in the Presence of Excess O2 over M@La–Fe/AC (M = Mn, Ce) Catalyst

Synthesis of Mn-Fe/γ-Al2O3 and Its Performance in Catalytic Oxidation of NO

Promotional effect for SCR of NO with CO over MnOx-doped Fe3O4 nanoparticles derived from metal-organic frameworks

Effect of Fe Reduced-Modification on TiO 2 Supported Fe–Mn Catalyst for NO Removal by NH 3 at Low Temperature

Iron, lanthanum and manganese oxides loaded on γ-Al2O 3 for selective catalytic reduction of NO with NH 3 at low temperature

Influence of the TiO2 Crystalline Phase of MnOx/TiO2 Catalysts for NO Oxidation

Iron, Lanthanum And Manganese Oxides Loaded On Gamma-Al2o3 For Selective Catalytic Reduction Of No With Nh3 At Low Temperature