Abstract:The activities of CuO supported on Ti0.5Zr0.5O2 have been examined with a microreactor-GC NO+CO reaction system and the catalysts characterized by BET, TPR,TG-DTA, XRD and NO-TPD. Experimental results show that the CuO/Ti0.5Zr0.5O2 activities increase with increase in CuO loading. To obtain 99% NO conversion, the reaction temperature needed to be 350degreesC in air but only 200degreesC in H-2 atmosphere. TPR analysis shows two peaks (alpha and beta peaks) at CuO loading of less than or equal to12%, while a third peak (gamma peak) occurs with higher CuO loading at 300degreesC. The alpha peak is attributed to highly dispersed CuO, the beta peak to isolated CuO and the gamma peak to crystal CuO. TG-DTA also shows endothermic peak at low temperature (120degreesC) and exothermic peak at high temperature (725degreesC), indicating the completion of ZrTiO4 crystallization. From the XRD analysis, it has been found that there is no CuO crystal diffraction peaks at 12% CuO loading, but two CuO crystal diffraction peaks at 2theta 35.5degrees and 38.7degrees are present at 18% CuO loading. With increase in CuO loading, the intensity of CuO diffraction peaks is increased. In addition, NO-TPD analysis shows that NO adsorption and desorption by Ti0.5Zr0.5O2 in air are similar to those in H-2 atmosphere. In air atmosphere, both CuO/Ti0.5Zr0.5O2 and Ti0.5Zr0.5O2 have two adsorption peaks, but the former has lower desorption peak temperature than the latter, suggesting that the activity of NO decomposition by CuO/Ti0.5Zr0.5O2 is higher than that by Ti0.5Zr0.5O2. In H, atmosphere, the high temperature desorption peak disappears and there only exists one low temperature desorption peak at 150degreesC, inferring that the high temperature adsorption site is probably Cu2+ and the low temperature adsorption site is Cu-0.

Comparative Study of Mn/Tio2 and Mn/Zro2 Catalysts for No Oxidation

Catalytic performance of MnO 2-CeO 2/Ti 0.25Zr 0.25Al 0.5O 1.75 monolith catalyst for low temperature selective catalytic reduction of NO with NH 3

Influence of the TiO2 Crystalline Phase of MnOx/TiO2 Catalysts for NO Oxidation

Comparative study on transition element doped Mn–Zr–Ti-oxides catalysts for the low-temperature selective catalytic reduction of NO with NH3

Mechanism Study Of No Catalytic Oxidation Over Mnox/Tio2 Catalysts

Mn-based catalysts supported on γ-Al 2 O 3 , TiO 2 and MCM-41: a comparison for low-temperature NO oxidation with low ratio of O 3 /NO

Effect of MnO(x) Modification on the Activity and Adsorption of CuO/Ce(0.67)Zr(0.33)O(2) Catalyst for NO Reduction.

MnOx/TiO2 Composite Nanoxides Synthesized by Deposition-Precipitation Method As a Superior Catalyst for NO Oxidation

Study of the Promotion Effect of Iron on Supported Manganese Catalysts for No Oxidation

Selective catalytic reduction of NOx with NH3 over Mn–Zr–Ti mixed oxide catalysts

ZrO 2 -Supported Α-Mno 2 :Improving Low-Temperature Activity and Stability for Catalytic Oxidation of Methane

A First-Principles Based Microkinetic Study of ZnMn1.5TM0.5O4 (TM = 3d Transition Metal) for NO Oxidation

Studies of Ti0.5zr0.5o2 Supported Cuo Catalysts for No+Co Reaction

Improved N2 Selectivity of MnOx Catalysts for NOx Reduction by Engineering Bridged Mn3+ Sites

Investigation of the active sites for NO oxidation reactions over MnOx–CeO2 catalysts

Catalyst Tolerance to SO2 and Water Vapor of Mn Based Bimetallic Oxides for NO Deep Oxidation by Ozone

Low-temperature selective catalytic reduction of NO on MnOx/TiO2 prepared by different methods

Comparative study of Mn oxide catalysts on toluene oxidation: The effect of Mn valence electronic structures

Enhanced low-temperature NO oxidation by iron-modified MnO2 catalysts

e to SO 2 and water vapor of Mn based bimetallic oxides for NO deep oxidation by ozone

Performance of surface oxygen over MnOx/ZrO2 catalysts