Abstract:Fe-Mn/TiO2 catalysts were prepared through the wet impregnation process to selective catalytic reduction of NO by NH3 at low temperature, and series of experiments were conducted to investigate the effects of key precursors on their SCR performance. Ferric nitrate, ferrous sulfate, and ferrous chloride were chosen as Fe precursors while manganese nitrate, manganese acetate, and manganese chloride as Mn precursors. These precursors had been commonly used to prepare Fe-Mn/TiO2 catalysts by numerous researchers. The results showed that there were distinct differences in NO conversion efficiencies at low temperature of catalysts prepared with different precursors. Catalysts prepared with ferric nitrate and manganese nitrate precursors exhibited the best catalytic performance at low temperature, while three kinds of catalysts prepared with manganese chloride precursors exhibited significantly low catalytic activity. All catalysts were characterized by XRD, SEM, H2-TPR, NH3-TPD, and XPS. The results indicated that when the catalysts were prepared with manganese nitrate or manganese acetate as precursors, Mn4+ contents and Oβ/(Oβ + Oα) ratios decreased in an order of ferric nitrate > ferrous sulfate > ferrous chloride, which was consistent with the change of catalytic activities of the corresponding catalysts at low temperature. It can be found that the excellent catalytic performance of Fe(A)-Mn(a)/TiO2 was ascribed to high redox property and enrichment of Mn4+species and surface chemical labile oxygen groups.

Effect of Preparation Condition on NO Removal Activity over Activated Carbon Honeycomb Supported MnOx Catalyst

Effect of Nitric Acid Pretreatment on the Properties of Activated Carbon and Supported Palladium Catalysts

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Activated Carbon Fibers Loaded with MnO2 for Removing NO at Room Temperature

Effect of pre-oxidation process on V2O5/AC catalyst for the selective catalytic reduction of NOx with NH3

Selective catalytic reduction of NOx with NH3 by monolithic catalyst MnOx/AC/C under low temperature in the presence of excess O2

Effect of MnO(x) Modification on the Activity and Adsorption of CuO/Ce(0.67)Zr(0.33)O(2) Catalyst for NO Reduction.

Effects of ferric and manganese precursors on catalytic activity of Fe-Mn/TiO2 catalysts for selective reduction of NO with ammonia at low temperature

Effects of Precursors on the Surface Mn Species and the Activities for NO Reduction over MnOx/TiO2 Catalysts

Preparation of Ag/ Al2O3 Selective Catalytic Reduction Monolithic Catalyst

Effect of preparation and reaction conditions on catalytic performances of honeycomb Pt/Al2O3

Insight into the promotion mechanism of activated carbon on the monolithic honeycomb red mud catalyst for selective catalytic reduction of NOx

Synthesis, characterization and catalytic performances of Cu- and Mn-containing ordered mesoporous carbons for the selective catalytic reduction of NO with NH3

Selective Catalytic Reduction of NO over Cu-Mn/OMC Catalysts: Effect of Preparation Method

Effects of precursors on the surface Mn species and SCR activities of MnOX/TiO2 catalysts

Low-temperature SCR of NO with NH3 over AC/C Supported Manganese-Based Monolithic Catalysts

Optimization of catalytic activity of MnCoOx catalyst for NH3–SCR at low temperature by response surface method

Mechanism of NO reduction by NH3 over MnCuOx catalysts and the influence mechanism of CO

In situ synthesis of low-valence MnO/Mn 3 O 4 catalyst via carbon-acid hydrothermal strategy for NO removal

Interactions between CO oxidation and selective catalytic reduction of NO with NH3 over Mn-based catalysts

Investigation and Characterization on MnO_x/TiO_2 for Low-Temperature Selective Catalytic Reduction of NO_x with NH_3