Abstract:In order to study the durability of concrete materials subjected to sulfate attack, in a sulfate attack environment, a series of concrete tests considering different fly ash contents and erosion times were conducted. The mechanical properties and the micro-structure of concrete under sulfate attack were studied based on the following: uniaxial compressive strength test, split tensile test, ultrasonic impulse method, scanning electron microscopy (SEM) and X-ray diffraction (XRD). The mechanical properties were compressive strength, splitting tensile strength, and relative dynamic elastic modulus, respectively. Additionally, according to the damage mechanical theory, experimental results and micro-structure analysis, the damage evolution process of concrete under a sulfate attack environment were studied in detail. Finally, according to the sulfate attack time and fly ash content, a damage model of the sulfate attack of the binary surface was established. The specific results are as follows: under the action of sulfate attack, the change law of the rate of mass change, relative dynamic modulus of elasticity, corrosion resistance coefficient of compressive strength, and the corrosion resistance coefficient of the splitting tensile strength of concrete all increase first and then decrease. Under the same erosion time, concrete mixed with 10% fly ash content has the best sulfate resistance. Through data regression, the damage evolution equation of the sulfate attack was developed and there is an exponential function relationship among the different damage variables. The binary curved surface regression effect of the concrete damage and the erosion time and the amount of fly ash is significant, which can predict deterioration of concrete damage under sulfate attack. During the erosion time, the combined expansion of ettringite and gypsum caused micro cracks. With an increase of corrosion time, micro cracks developed and their numbers increased.

Overview of Concrete Durability under Sulfate Attack and Multi-Factor Coupling Effects

Research on the performance evolution of concrete under the coupling effects of sulfate attack and carbonation

Damage Mechanism of Concrete Deteriorated by Sulfate Attack in Wet-Dry Cycle Environment

Concrete Deterioration Mechanisms under Combined Sulfate Attack and Flexural Loading

Effect of Multiple Ions on the Degradation in Concrete Subjected to Sulfate Attack

Experimental study of the deterioration mechanism of concrete under sulfate attack in wet-dry cycles

Review of Sulfate Attack on Concrete

Chloride penetration in concrete exposed to cyclic drying-wetting and carbonation

Mechanical Properties and Damage Evolution of Concrete Materials Considering Sulfate Attack

Combined effects of sulfate attack under drying–wetting cycles and loading on the fatigue behavior of concrete

Effects of Sodium Sulfate Attack on Concrete Incorporated with Drying-Wetting Cycles

Research on the Sulfate-resistant Chemical Attack Mechanism of Concrete with Mineral Admixture

Compressive Strength Assessment of Sulfate-Attacked Concrete by Using Sulfate Ions Distributions

Modeling of Concrete Deterioration under External Sulfate Attack and Drying-Wetting Cycles: A Review

Mechanism and Performance Control Methods of Sulfate Attack on Concrete: A Review

Investigation of concrete exposed to dual sulfate attack

Reliability assessment of concrete under external sulfate attack

Experimental study on underground structure concrete under static bending loads and sulfate attack

A Review on the Transport-Chemo-Mechanical Behavior in Concrete under External Sulfate Attack

Damage Constitutive Model and Mechanical Performance Deterioration of Concrete under Sulfate Environment

Numerical Investigation of External Sulfate Attack and Its Effect on Chloride Binding and Diffusion in Concrete