Abstract:Cast-in-situ concrete suffers complicated working conditions in sulfate-rich saline soil areas. Sulfate-magnesium combined attack can be encountered in heavy saline or salty lake areas. This study investigated the degradation process and corresponding mechanisms of cast-in-situ concrete, contaminated by chlorides, partially exposed to sulfate-magnesium combined corrosive environments. Concrete samples were cast and partially immersed in the pre-prepared distilled water, sulfate or sulfate-magnesium mixed solutions for 12 months. Physical and mechanical properties of concrete samples were continuously measured and recorded during the immersion. Sulfate concentration in different depths were measured by chemical titration. SEM, XRD, TG/DTG tests were conducted to analyze the microstructural and mineral property changes after corrosion for concrete suffered different corrosion conditions. Results show that partially immersed concrete encounters both chemical and physical degradation induced by corrosive sources. Concrete contaminated by chlorides obviously shows weaker resistance against sulfate attack and the strength development is also negatively affected. Magnesium in the environments reduces the early strength of partially immersed cast-in-situ concrete while enhancing the sulfate resistance ability in the later corrosion stage. Magnesium limits the negative effect of contaminated chlorides on the partially immersed cast-in-situ concrete. Performance of cast-in-situ concrete is different from precast concrete when encountering different corrosive sources, and thus more attention should be paid on the degradation of cast-in-situ concrete structures induce by aggressive environments.

Investigation of concrete exposed to dual sulfate attack

Sulphate attack resistance of high-performance concrete under compressive loading

Durability of self-consolidating concrete to different exposure regimes of sodium sulfate attack

Sulfate attack on concrete with mineral admixtures

Deterioration Mechanisms of Ultra-High-Performance Concrete Under Various Sulfuric Acid and Sulfate Attack Conditions

Research on the Sulfate-resistant Chemical Attack Mechanism of Concrete with Mineral Admixture

Experimental study of the deterioration mechanism of concrete under sulfate attack in wet-dry cycles

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Damage Mechanism of Concrete Deteriorated by Sulfate Attack in Wet-Dry Cycle Environment

Degradation Mechanisms of Chloride Contaminated Cast-in-Situ Concrete Partially Exposed to Magnesium-Sulfate Combined Environment

Overview of Concrete Durability under Sulfate Attack and Multi-Factor Coupling Effects

Effects of Sodium Sulfate Attack on Concrete Incorporated with Drying-Wetting Cycles

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Concrete Deterioration Mechanisms under Combined Sulfate Attack and Flexural Loading

Partially-exposed cast-in-situ concrete degradation induced by internal-external sulfate and magnesium multiple coupled attack

Deterioration Mechanisms of Sulfate Attack on Concrete under Alternate Action

Degradation Mechanism of Concrete Subjected to External Sulfate Attack: Comparison of Different Curing Conditions

Reliability assessment of concrete under external sulfate attack

Mechanism and Performance Control Methods of Sulfate Attack on Concrete: A Review

Investigation on durability of concrete exposed to chloride, sulfate attack and steel corrosion

Effect of an Early-Age Exposure on the Degradation Mechanisms of Cement Paste under External Sulfate Attack