Influence of CNTs on the Sintering Behavior and Mechanical Properties of Boron Carbide by SPS Process

WEI Hong-kang,ZHAO Lin,WANG Chang-an,XIE Zhi-peng,DENG Xiang-yu

2014-01-01

Abstract:CNTs / B4 C ceramic matrix composites were prepared by spark plasma sintering at 1600 ℃under 50 MPa. The effects of CNTs additions on the sintering behavior and mechanical properties of B4 C were studied. The phase composition and microstructure of the composites were analyzed by XRD and SEM. The results indicate that the relative density and mechanical properties first increases as the CNTs contents increasing,and thereafter decreases. As the CNTs content was 1wt%,the maximum relative density and mechanical properties were obtained. The appropriate content of CNTs were beneficial for the powder sliding during the sintering process,resulting in the improvement of density. As the CNTs contents increasing,the density decreased,due to the obvious space steric hindrance.