Abstract:In order to achieve desired mechanical properties of alloys by manipulating grain boundaries (GBs) via solute decoration, it is of great significance to understand the underlying mechanisms of microstructural evolution and plastic deformation. In this work, nanocrystalline (NC) Cu-W alloyed films with W concentrations spanning from 0 to 40 at% were prepared by using magnetron sputtering. Thermal stability (within the temperature range of 200 °C-600 °C) and hardness of the films were investigated by using the x-ray diffraction, transmission electron microscope (TEM) and nanoindentation, respectively. The NC pure Cu film exhibited substantial grain growth upon all annealing temperatures. The Cu-W alloyed films, however, displayed distinct microstructural evolution that depended not only on the W concentration but also on the annealing temperature. At a low temperature of 200 °C, all the Cu-W alloyed films were highly stable, with unconspicuous change in grain sizes. At high temperatures of 400 °C and 600 °C, the microstructural evolution was greatly controlled by the W concentrations. The Cu-W films with low W concentration manifested abnormal grain growth (AGG), while the ones with high W concentrations showed phase separation. TEM observations unveiled that the AGG in the Cu-W alloyed thin films was rationalized by GB migration. Nanoindentation results showed that, although the hardness of both the as-deposited and annealed Cu-W alloyed thin films monotonically increased with W concentrations, a transition from annealing hardening to annealing softening was interestingly observed at the critical W addition of ∼25 at%. It was further revealed that an enhanced GB segregation associated with detwinning was responsible for the annealing hardening, while a reduced solid solution hardening for the annealing softening.

Influence of Heating Rate on Formation of Nanostructured Tungsten Carbides During Thermo-Chemical Processing

Nanostructured Tungsten Carbides by Thermochemical Processing

Atomic Scale Stability of Tungsten-Cobalt Intermetallic Nanocrystals in Reactive Environment at High Temperature.

Effect of High Temperature Annealing on the Microstructure and Thermal Shock Resistance of Tungsten Coatings Grown by Chemical Vapor Deposition

Influence of Surface Morphology and Microstructure on Performance of CVD Tungsten Coating under Fusion Transient Thermal Loads

Stability of Nanostructured W-C Phases During Carburization of WO3

Effect of Heating Rate on the Morphology of Nano Titanium Dioxide

Study on influencing factors and mechanism of high-quality tungsten carbide nanopowders synthesized via carbothermal reduction

Novel synthesis of hierarchical tungsten carbide micro-/nanocrystals from a single-source precursor

The W alloying effect on thermal stability and hardening of nanostructured Cu-W alloyed thin films

Tungsten carbide (WC) nanopowders synthesized via novel core–shell structured precursors

Structure and orientation of an intermetallic phase in a W-Ni-Co alloy

Evaluation of microstructure and growth kinetics of tungsten carbide ceramics at the interface of iron and tungsten

Synthesis of nano (Ti,W)C powder with preferred orientation and twin boundary structure

The Synthesis of Nanostructured W2c on Ultrahigh Surface Area Carbon Materials Via Carbothermal Hydrogen Reduction

Structural Stability of Α/β-Mo2c During Thermochemical Processing

A Tungsten-Based Nanolaminated Ternary Carbide: (W,Ti)4C4- x

Observable Two-Step Nucleation Mechanism in Solid-State Formation of Tungsten Carbide.

Formation of tungsten carbide by focused ion beam process: A route to high magnetic field resilient patterned superconducting nanostructures

Tungsten Matrix Composite Reinforced with CoCrFeMnNi High-Entropy Alloy: Impact of Processing Routes on Microstructure and Mechanical Properties

Effect of Ball Milling Parameters on Properties of Nano-Sized Tungsten Powder via Mechanochemical Processing