Abstract:In this work, the WC-Cr2(C, N)-Co nanocomposites were synthesized by using the one-pot carbothermal reduction nitridation hydrothermal precursor method. The preparation mechanisms, including phase and morphology evolutions, were investigated by differential thermal analysis (TG-DSC), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and thermodynamic analysis. The results showed that phase evolution, with temperature increasing, follows the sequences of (amorphous phase, WO2.72) → (CoWO4, WO2.72, WO2, CrWO3) → (WO2, CoWO4, Co6W6C, CrWO3) → (W2C, Co3W3C, WC) → (WC, W2C, Co3W3C) → (WC, Co, Co3W3C trace amount). Through comparing different heat treatment conditions, the powder particle size was more easily affected by temperature than holding time. The higher temperatures or longer time holding resulted in the aggregation of powder particles. Finally, WC-Cr2(C, N)-Co nanopowders with about 60 nm were obtained at 1050 °C for 1 h under the N2 flow of 1 L/min with the oxygen content of 0.22 wt% and the free carbon content of 0.19 wt%. The TEM elements mapping revealed that Cr distributes uniformly with WC grains, Co and WC grains are combined well. The surface of WC-Cr2(C, N)-Co determined by XPS is mainly composed of W, Co, Cr, C, N, and O. The spark plasma sintering (SPS) sintered WC-Cr2(C, N)-Co composite shows a nanocrystalline microstructure with the average grain size ∼170 nm, and the excellent comprehensive mechanical properties with the Vickers hardness 1730 Kg·mm−2 and fracture toughness 11.5 MPa·m1/2, respectively.

Nanostructured Tungsten Carbides by Thermochemical Processing

Stability of Nanostructured W-C Phases During Carburization of WO3

Influence of Heating Rate on Formation of Nanostructured Tungsten Carbides During Thermo-Chemical Processing

Atomic Scale Stability of Tungsten-Cobalt Intermetallic Nanocrystals in Reactive Environment at High Temperature.

Synthesis of Nanostructured Tungsten Carbide (WC) from Ammonia Paratungstate-APT and its Characterization by XRD and Rietveld Refinement

Novel synthesis of hierarchical tungsten carbide micro-/nanocrystals from a single-source precursor

Tungsten carbide (WC) nanopowders synthesized via novel core–shell structured precursors

Structural Stability of Α/β-Mo2c During Thermochemical Processing

The Synthesis of Nanostructured W2c on Ultrahigh Surface Area Carbon Materials Via Carbothermal Hydrogen Reduction

Synthesis of nano (Ti,W)C powder with preferred orientation and twin boundary structure

Synthesis of WC-0.67wt.%Cr3C2 nanopowders by a one-step reduction-carbonization method and their characterization

A Tungsten-Based Nanolaminated Ternary Carbide: (W,Ti)4C4- x

Study on the preparation mechanism of novel WC-Cr2(C, N)-Co nanocomposites

Preparation of nano-scaled WC powder by low-temperature carbothermic reduction method

Ultrafine and Nanoscaled Tungsten Carbide Synthesis from Colloidal Carbon Coated Nano Tungsten Precursor

Study on influencing factors and mechanism of high-quality tungsten carbide nanopowders synthesized via carbothermal reduction

Structure and orientation of an intermetallic phase in a W-Ni-Co alloy

Controllable preparation of tungsten/tungsten carbide nanowires or nanodots in nanostructured carbon with hollow macroporous core/mesoporous shell

Synthesis of Tungsten Carbide Nanocrystal Via A Simple Reductive Reaction

Synthesis of Metastable Ternary Pd-W and Pd-Mo Transition Metal Carbide Nanomaterials

Preparation of Nanoscale WC Powders by Sol-Gel Synthesis and Carbon Monoxide Carbonization