Abstract:Recently, there is the serious fracture for two high-temperature steam turbine rotors made of 30Cr1Mo1V steel in different power plants, characterized by brittle fracture. This steel has the disadvantage of low temperature brittleness. Currently, a large number of 30Cr1Mo1V rotors are in service. Meanwhile, these rotors are required to start up and warm up faster due to the demand for operation flexibility of the power system. In order to ensure the safety of the 30Cr1Mo1V rotors under flexible operation, it is necessary to study the low temperature brittleness of the rotors and its influence on the fatigue life in rapid start-up and warm-up processes. In this paper, the fracture causes of the 30Cr1Mo1V rotor were analyzed by the mechanical property tests, microstructure examination and fracture analysis. The test results showed that the toughness of rotor decreased significantly after service. Secondly, the temperature and stress changes of the high-temperature rotors during the rapid start-up and warm-up process were calculated by the finite element method. The simulation results showed that if the speed rose too fast, the thermal stress in the rotor inlet area would increase significantly and the temperature was lower than the fracture appearance transition temperature when reaching the full speed. The high stress will easily lead to a crack initiation under low-cycle fatigue. Then, crack instability propagation will soon occur due to the low temperature and poor toughness. Thirdly, the life of the turbine in the rapid start-up was optimized by controlling the startup time. In addition, the life under different warm-up conditions was quantitatively analyzed. It not only reveals the necessity of the warm-up process for the center hole rotor, but also successfully demonstrates that the warm-up process of the solid rotor can be cancelled, which improves the economy of the power plant.

Temperature rise rate of steam turbine at cold-state start-up considering the hardness changes of rotor materials

Optimization of Start-up Process in Combined Cycle Steam Turbine of a Power Plant

Study on Quick Start-up of Steam Turbine in a Gas-Steam Combined Cycle

Research on low temperature brittleness of 30Cr1Mo1V high-temperature rotor and its life optimization in rapid start-up and warm-up process

Evaluation of Thermodynamic State of Rotor Under In-Service Operating Conditions

Calculation of Finite Element of Thermal Stress and Analysis of Low-cyclic Fatigue Life for Non-central Hole Rotor of 135 MW Turbine

Life Estimation for Transient Temperature and Stress Field of Heavy-duty Gas Turbine Rotor

Optimization on Start-up Process of Steam Turbine in Combined Cycle Generating Units

Research on Optimization of Intermediate Pressure Cylinder Start Process for 600MW Unit

Numerical Investigation on Life Improvement of Low-Cycle Fatigue for an Ultra-Supercritical Steam Turbine Rotor

Stress Analysis and Life Assessment of the Steam Turbine Rotor During Peak Shaving Transient Processes

Optimization and Experiment Study on Start-up Temperature Control Curve of Turbine Rotor

Transient Analysis and Design Improvement of a Gas Turbine Rotor Based on Thermal-Mechanical Method

A Study of the Establishment of Turbine Rotor Steam-cooling Calculation Models

Transient Characteristics Analysis of Thermal-Stress in Start-Stop Condition for Rotor System in Gas Turbine

C206 A METHOD EVALUATING SERVICE LIFE OF STEAM TURBINE ROTOR BASED ON ARTIFICIAL NEURAL NETWORK

Optimization on Start-Up Process of High-Pressure Rotor for Large Power Steam Turbine

Damage Analysis and Start-Up Schedule Optimization of Steam Turbine Rotors With an Anisotropic Damage Coupled Viscoplastic Constitutive Model

Influence of High-Temperature Dwell Time on Creep-Fatigue Behavior in A 1000 Mw Steam Turbine Rotor

Material Degradation And Creep Damage Of Aging Components At High Temperature

Fatigue life prediction of a supercritical steam turbine rotor based on neural networks