Abstract:In this paper, high-quality nanosized Ce 0.8 Sm 0.2− x Zn x O 2− δ ( x = 0, 0.02, 0.04, 0.08, and 0.16) powders are successfully synthesized by sol–gel process for intermediate-temperature solid oxide fuel cell (IT-SOFC) application. The thermal behavior, porosity, crystal phase, surface microstructure, and electrical properties of Ce 0.8 Sm 0.2− x Zn x O 2− δ are studied by thermogravimetric-differential scanning calorimeter (TG-DSC), Archimedes drainage method, X-ray diffraction (XRD), scanning electron microscope (SEM), and electrochemical impedance spectroscopy (EIS), respectively. The results show that Ce 0.8 Sm 0.2− x Zn x O 2− δ electrolyte appears very high sintering activity even at sintering temperature as low as 1300 °C. The crystal phase of sample powders after sintered at 600 °C belongs to single-phase cubic fluorite structure with mean particle size of 15 nm. The lattice parameter increases first until doping 2 mol.% Zn and then decreases with more doping amount. Electrochemical performance results demonstrate that doping with appropriate amount of Zn can significantly improve the conductivity of SDC materials. The highest conductivity of 0.057 S·cm −1 at 800 °C is obtained for Ce 0.8 Sm 0.16 Zn 0.04 O 2− δ , owing to high density, ultrafine grains, and increased grain boundaries. Furthermore, the fuel cell performance of Ce 0.8 Sm 0.16 Zn 0.04 O 2− δ electrolyte is measured with 5 wt.% Fe-loaded activated carbon as the fuel. It delivers an outstanding performance, with an OCV of 1.02 V, a maximum power output of 408 mW·cm −2 at 850 °C, indicating that Ce 0.8 Sm 0.16 Zn 0.04 O 2− δ may have potential application for IT-SOFC electrolyte materials.

Preparation of anode supported thin electrolytes for IT-SOFCS

A simple and easy one-step fabrication of thin BaZr0.1Ce0.7Y0.2O3−δ electrolyte membrane for solid oxide fuel cells

Preparation of Thin Electrolyte Film Via Dry Pressing/heating/ Quenching/calcining for Electrolyte-Supported SOFCs

Fabrication and Performance of Anode-Supported Electrolyte Thin Films SOFCs

Electrophoretic Deposition in the Preparation of Electrolyte Thin Films for Solid Oxide Fuel Cells

Application of Novel Aerosol-Assisted Chemical Vapor Deposition Techniques for SOFC Thin Films

Scalable and facile fabrication of tri-layer electrolytes by reactive sputtering for efficient and durable solid oxide fuel cells

Direct Electrophoretic Deposition and Characterization of Thin-Film Membranes Based on Doped BaCeO3 and CeO2 for Anode-Supported Solid Oxide Fuel Cells

Electrophoretic deposition of YSZ thin-film electrolyte for SOFCs utilizing electrostatic-steric stabilized suspensions obtained via high energy ball milling

A cathode-supported SOFC with thin Ce0.8Sm0.2O1.9 electrolyte prepared by a suspension spray

Fabrication and Properties of Anode-Supported Solid Oxide Fuel Cell

Direct synthesis of Ce0.8Sm0.2−xZnxO2−δ electrolyte by sol–gel for IT-SOFC

Improvement of Anode-Supported Solid Oxide Fuel Cells

Hierarchically oriented macroporous anode-supported solid oxide fuel cell with thin ceria electrolyte film.

Sintered powder-base cathode over vacuum-deposited thin-film electrolyte of low-temperature solid oxide fuel cell: Performance and stability

Fabrication and Characterizations of Ysz Electrolyte Films for Sofc

Fabrication and Characterization of Composite Electrolyte for Intermediate-Temperature SOFC

Fabrication of Electrode Supporters for Solid Oxide Fuel Cells by Tape Calendaring Process

Boosting intermediate temperature performance of solid oxide fuel cells via a tri‐layer ceria–zirconia–ceria electrolyte

Nanocrystal Engineering of Thin-Film Yttria-Stabilized Zirconia Electrolytes for Low-Temperature Solid-Oxide Fuel Cells

Optimization of ScSZ/GDC bilayer thin film electrolyte for anodic aluminum oxide supported low temperature solid oxide fuel cells