Abstract:Magnesium oxide (MgO) thin films with different magnesium concentrations ([Mg2+] = 0.05, 0.1, 0.15 and 0.2 mol·L−1) in a spray solution have been successfully grown using a spray pyrolysis technique. X-ray diffraction (XRD), Maud software, FTIR spectroscopy, a confocal microscope, Wien2k software, spectrophotometry and a Photoluminescence spectrometer were used to investigate the structural, morphological and optical properties. XRD analysis revealed a better crystalline quality of the MgO thin layer synthesized with [Mg2+] = 0.15 mol·L−1, which crystallized into a face-centered cubic structure along the preferred orientation (200) lattice plan. The enhancement of the crystalline quality for the MgO thin film ([Mg2+] = 0.15 mol·L−1) was obtained, which was accompanied by an increment of 94.3 nm of the crystallite size. No secondary phase was detected and the purity phase of the MgO thin film was confirmed using Maud software. From the transmission spectra results, high transparent and antireflective properties of the MgO thin film were observed, with an average transmission value of about 91.48% in the visible range, which can be used as an optical window or buffer layer in solar cell applications. The films also have a high reflectance value in the IR range, which indicates that the highly reflective surface will prevent an increase in surface temperature under solar irradiation, which could be beneficial in solar cell applications. A direct band gap type was estimated using the Tauc relation which is close to the experimental value of 4.0 eV for optimal growth. The MgO material was tested for the degradation of methylene blue (MB), which reached a high photodegradation rate of about 83% after 180 min under sunlight illumination. These experimental trends open a new door for promising the removal of water contaminants for photocatalysis application.

Investigation of Thermal Stability of Atomic-Layer-Deposited MgO Thin Films on Si(100) Using X-Ray Photoelectron Spectroscopy

Preparation and Characterization of Mg-doped ZnO Thin Films by Sol–gel Method

Thermal Stability of Mg 2 Si Epitaxial Film Formed on Si (111) Substrate by Solid Phase Reaction

Enhanced photocatalytic activity of Mg 0.05 Zn 0.95 O thin films prepared by sol–gel method through a cycle

Microstructue and Optical Properties of Mg-doped ZnO Thin Films Prepared by Sol-gel Method

Annealing effect on electrical properties of high-k MgZnO film on silicon

X-ray Photoelectron Spectroscopy Study of ZnO Films Grown by Metal-Organic Chemical Vapor Deposition

Effects of Post-Annealing Treatment on the Structural and Optical Properties of Cubic Mg Chi Zn1-Chi O Thin Films Grown on Sapphire

Elaboration and Characterization of Mg-Doped ZnO Thin Films by Thermal Evaporation: Annealing Temperature Effect

Effect of annealing on optical properties of Mg(x)Zn(1-x)Othin films deposited at low temperature

Characterizations of Cubic ZnMgO Films Grown on Si(111) at Low Substrate Temperature

[Effects of Annealing Temperature on the Structure and Optical Properties of ZnMgO Films Prepared by Atom Layer Deposition].

Deposition And Microstructural Characterization Of Mgo Thin Films By A Spray Pyrolysis Method

GROWTH OF MgO THIN FILMS ON Si SUBSTRATES BY MAGNETRON SPUTTERING

Orientation of MgO thin films grown by pulsed laser deposition

Interfaces of Mg and Mgox Films with Gaas(100) Substrate Studied by Synchrotron Radiation Photoemission

Crystallographic Texture of MgO and its Effect on the Growth of BaTiO<sub>3</sub> Thin Films by RF Sputtering

Physics and chemistry during the deposition and oxidation of ultrathin Mg overlayer on GaAs(100) surface

The deposition and annealing study of MOCVD ZnMgO

Synthesis and Characterization of MgO Thin Films Obtained by Spray Technique for Optoelectronic Applications

Heteroepitaxial Growth of MgO Films by Dual Ion Beam Sputtering