Abstract:Al-Zn-Mg-Cu alloy, as an important lightweight structural material in the aerospace field, has ushered in a broader application space and proposed higher performance requirements. This paper presents the experimental investigation of the effect of Zr content on the microstructure refinement and performance improvement of cast Al-5.8Zn-2.3Mg-1.7Cu alloy, aiming to optimize the additional amount of Zr, refine the alloy grains, and improve the microstructure uniformity and mechanical properties. The chemical component, phase, and microstructure were observed by inductively coupled plasma, X-ray diffraction, optical microscope and scanning electron microscope; the hardness and mechanical properties were measured by Brinell hardness tester and tensile testing machine. The addition of different contents of Zr into the alloy can form fine dispersed or primary coarse Al3Zr phase, which has a significant effect on the microstructure and mechanical properties of the alloy. The results indicate that the addition of 0.05 wt% Zr does not significantly improve the grain refinement and mechanical properties, but the Brinell hardness reaches the maximum. As the Zr content rises, the grain refinement effect becomes more obvious, while the mechanical properties first increase and then decrease. The addition amount reaches 0.20 wt%, the second dendrite arm spacing is the smallest, the ultimate tensile strength, yield strength and elongation at room temperature reach the maximum of 296.74 MPa, 249.41 MPa and 8.26%, respectively. When the amount of Zr added exceeds 0.20 wt%, the existence of coarse and brittle primary Al3Zr phase reduces the mechanical properties, and the fracture morphology changes from ductile to brittle intergranular fracture.

Effect of Sc and Zr on the In-Plane Anisotropy of Al-Mg-Mn Alloy Sheets

Microstructures and Properties of Al–Zn–Mg–Mn Alloy with Trace Amounts of Sc and Zr

Effect of Sc/Zr ratio on the microstructure and mechanical properties of new type of Al–Zn–Mg–Sc–Zr alloys

Effect of Icosahedral Phase on Crystallographic Texture and Mechanical Anisotropy of Mg–4%Li Based Alloys

Effects of Icosahedral Phase on Mechanical Anisotropy of As-Extruded Mg-14Li (in Wt%) Based Alloys

Effect of Zr addition on the microstructure evolution and mechanical properties of extruded Al-Cu-Li-Mn alloys

Effects of Zn Addition and Twin Roll Casting Process on the Microstructure, Texture, and Mechanical Properties of the Mg-Al-Mn-Ca Sheet

Effect of grain thickness and T 1 precipitate on the strength anisotropy of Al-4.0Cu-1.0Li-0.4Mg-0.4Ag-xZr alloys under different heat treatment

Effect of Icosahedral Phase on the Crystallographic Texture and Mechanical Anisotropy of Duplex Structured Mg–Li Alloys

Effect of Sc contents on the mechanical properties and damping capacity of Al-Zn-Mg-Cu-Zr-Sc alloys with different grain structures

Ab initio study of the effect of Zr content on elastic and electronic properties of L12–Al3(Sc1−xZrx) alloys

Effect of minor Sc and Zr on recrystallization behavior and mechanical properties of novel Al–Zn–Mg–Cu alloys

Effects of Zr+Er and Zr+Y on Microstructure and Tensile Properties of Al-Mg-Si-Cu-Mn-Cr Alloys

Influences of different Zr/Sc ratios on microstructure and mechanical properties of Al-2Si alloy

Effect of Sc microalloying on microstructure evolution and mechanical properties of extruded Al-Zn-Mg-Cu alloys

Effect of Microstructure and Texture on the Mechanical Properties of the As-Extruded Mg–Zn–Y–Zr Alloys

Effect of Sc and Zr on Microstructure and Mechanical Properties of As‐Cast Al–Li–Cu Alloys

Effects of Extrusion Ratio on the Microstructure, Texture and Mechanical Properties of Mg-2.5Nd-0.5Zn-0.5Zr Alloy Sheets

Effect of Sc and Zr on recrystallization behavior of 7075 aluminum alloy

Influence of Zr content on microstructure and mechanical properties of As-cast Al-Zn-Mg-Cu alloy

Influence of Sc and Zr additions on microstructure and properties evolution of Al–Zn–Mg alloy