Effect of Mg-Based Quasicrystals Addition on Microstructure and Mechanical Properties of AM50 Magnesium Alloy

Ma Dezhi,Wang Feng,Wang Zhi,Liu Zheng,Mao Pingli

2018-01-01

Rare Metal Materials and Engineering

Abstract:The Mg-48Zn-13Y (MZY) quasicrystal master alloy with high volume fraction of the quasicrystalline phase was prepared by a conventional solidification method. The influences of the MZY quasicrystal on microstructures and mechanical properties of AM50 alloys were investigated by OM, SEM, EDS, XRD and tensile tests. The results indicate that with addition of the MZY quasicrystal to AM50 alloy, the Mg3Zn6Y quasicrystal phase can be retained in AM50 matrix alloy, and the microstructures are obviously refined. The beta phase in the microstructures is changed from coarse and continuous net-like to discontinuous strip-like and granular, and the amount is decreased. When the content of the MZY quasicrystal is 6%, the microstructure is greatly refined, and the ultimate tensile strength, yield strength and elongation of the alloy reach to the maximum, 202.92 MPa, 100.57 MPa and 10.8%, respectively, which are improved by 24.59%, 74.9% and 66.15%, respectively, compared with those of AM50 alloy. Mechanical properties of AM50 magnesium alloy can be improved significantly by addition of the MZY quasicrystal, which results from the microstructure refinement, the optimization of the morphology and amount of the beta phase, and the dispersion strengthening effect of the quasicrystal phase having good wettability with the magnesium alloy substrate.