Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

Improvement of microstructure and mechanical properties of Mg–8Gd–3Y by adding Mg3Zn6Y icosahedral phase alloy

Microstructure and Interface of Mg3Zn6Y Quasicrystal Particulate Reinforced Mg-8Gd-3Y Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Microstructure and Interface Of Mg<sub>3</sub>Zn<sub>6</sub>Y Quasicrystal Particulate Reinforced Mg-8Gd-3Y Alloy

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Microstructure and properties of Mg-based quasicystal particulate reinforced composite

Microstructure and Phase Transformation of Forged Mg–3.7Zn–0.3Y–0.3Gd Quasicrystal Alloy

Microstructure and Mechanical Properties of Mg-Zn-Gd-Based Alloys Strengthened with Quasicrystal and Laves Phase

Microstructure and mechanical properties of Mg-12Gd-5Y-1Sm-0.5Zr alloy

Microstructure and Mechanical Properties of Mg-12Gd-2Y-1.5Sm-0.5Zr Alloy

Microstructure and Mechanical Properties of As-Cast and Solution-Treated Mg-Zn-Gd-based Alloys Reinforced with Quasicrystals

Microstructure and mechanical properties of cast Mg-6Gd–Zr alloy with different Y addition

Crystal structure, phase content, and tensile properties of As-cast Mg–Gd–Y–Al alloys

Microstructure Evolution and Mechanical Properties of Quasicrystal-Reinforced Mg–Zn–Gd Alloy Processed by Cyclic Extrusion and Compression

Effect of Zn and Y on microstructures and properties of normally-solidified Mg-Zn-Y alloys

The Partial Substitution of Y with Gd on Microstructures and Mechanical Properties of As-Cast and As-Extruded Mg-10Zn-6Y-0.5Zr Alloy

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Effect of Yb Addition on the Microstructure and Mechanical Properties of the Mg–4Sm–3Gd–0.5Zr Alloy

Microstructure and properties of Mg-9Gd-4Y-1Zn-0.5Zr alloy

The Effect of Gd and Zn Additions on Microstructures and Mechanical Properties of Mg-4sm-3nd-Zr Alloy

Microstructures and Mechanical Properties of the Mg–4.5Zn–xGd (x = 0, 2, 3 and 5) Alloys