Abstract:In this study, equal channel angular pressing (ECAP) was applied to a hot-extruded Mg–5.00Zn–0.92Y–0.16Zr (wt.%) alloy to produce an ultrafine-grained a-Mg structure of 0.6μm with uniformly distributed fine quasicrystal Mg3YZn6 particles. The basal planes in the as-ECAPed alloy were inclined approximately 45° to the ECAP direction (EPD); thus, a high Schmid factor of 0.36 for (0001)〈112¯0〉 basal slip along EPD was obtained. Then, the superplastic behavior at low temperatures of 150–250°C and initial strain rates of 1.67×10−3s−1–1.67×10−1s−1 of the as-ECAPed alloy was investigated and compared with that of the as-extruded alloy. The microstructural development, texture evolution and cracking behavior during tensile tests were systemically investigated by electron backscattered diffraction (EBSD) analysis. During the tensile test along the EPD, the basal planes in the as-ECAPed alloy specimen were tilted approximately 15° away from the original position; thus, the basal planes were still in a position favorable for the basal slip along the EPD. As a result, a maximum elongation of 865% was obtained at 200°C and a strain rate of 1.67×10−3s−1, as a result of this favored basal texture and the excellent thermal stability of the ultrafine-grained structure. This optimum superplastic temperature of 200°C is much lower than that obtained for other Mg–Zn–Y–(Zr) alloys. In contrast, for the as-extruded alloy specimen, superplastic behavior did not occur until the critical condition of 250°C and a strain rate of 1.67×10−3s−1. Below this temperature and strain rate, the strong extrusion basal texture was maintained, and the cracks in the hot-worked coarse region (or un-DRXed region) were observed nucleating mainly associated with the formation of a 38° {101¯1}–{101¯2} double twin. At this temperature and strain rate, the hot-worked coarse regions were significantly refined by the dynamic recovery and the following recrystallization process. In the case, the formation of a double twin was prevented and the facture was delayed.

Effect of Hot Extrusion on Microstructure and Mechanical Properties of Quasicrystal-Reinforced Mg-Zn-Y Alloy

Microstructure and Mechanical Properties of Extruded Mg-Zn-Y Alloy

The effect of nanoquasicrystals on mechanical properties of as-extruded Mg-Zn-Gd alloy

Effects of extrusion on the microstructure and mechanical properties of Mg–Zn–Gd alloy reinforced with quasicrystalline particles

Recrystallization and Microstructural Evolution During Hot Extrusion of Mg 97 Y 2 Zn 1 Alloy

Effect of Extrusion Parameters on Microstructure and Mechanical Properties of Mg-7.5Gd-2.5Y-3.5Zn-0.9Ca-0.4Zr (wt%) Alloy

Hot Extrusion Effect on the Microstructure and Mechanical Properties of a Mg–Y–Nd–Zr Alloy

Hot Compression Deformation Behavior of Mg-Zn-Al-(Y) Alloys Reinforced with Quasicrystal

Effect of Icosahedral Quasicrystalline Fraction and Extrusion Ratio on Microstructure, Mechanical Properties, and Anisotropy of Mg-Zn-Gd-Based Alloys

The Role of Nanoquasicrystals on the Ductility Enhancement of As-Extruded Mg–Zn–Gd Alloy at Elevated Temperature

Effect of quasicrystal and Laves phases on strength and ductility of as-extruded and heat treated Mg–Zn–Gd-based alloys

Effect of Microstructure and Texture on the Mechanical Properties of the As-Extruded Mg–Zn–Y–Zr Alloys

The Microstructural Evolution and Superplastic Behavior at Low Temperatures of Mg–5.00Zn–0.92Y–0.16Zr (wt.%) Alloys after Hot Extrusion and ECAP Process

Dynamic Microstructural Changes During Hot Extrusion and Mechanical Properties of a Mg–5.0 Zn–0.9 Y–0.16 Zr (wt.%) Alloy

Effect of Zn and Y on microstructures and properties of normally-solidified Mg-Zn-Y alloys

Microstructure and Mechanical Properties of Extruded Mg-Zn-Nd-Y-Zr-Ca Alloy

Evolution of Microstructure and Tensile Properties of Extruded Mg-4Zn-1Y Alloy

Effect of Artificial Cooling Extrusion on Microstructure and Mechanical Properties of Mg–Zn–Y Alloys

Microstructure and Tensile Properties of As-Extruded Mg–Li–Zn–Gd Alloys Reinforced with Icosahedral Quasicrystal Phase

Effects of extrusion process on microstructure, precipitates and mechanical properties of Mg-Gd-Y-Zr-Ag alloys

Microstructure and Mechanical Properties of Mg–4Zn–xY Alloys Prepared by Hot-Extrusion