Abstract:Solid particle erosion wear behavior of 3YSZ ceramics were performed by self-designed sand blasting type high-temperature solid particle erosion wear equipment, using 36#corundum as abrasive particles. 3YSZ ceramics were pressureless sintered in air atmosphere at 1500°C for 3h. The fracture toughness and Vickers hardness could achieve 10.3 MPa•m1/2and 12.8 GPa, respectively. The effect of temperature (25°C, 400°C, 600°C, 800°C, 1000°C) and the total weight of the abrasive particles (300g, 900g, 1800g) at room temperature on the erosion wear of 3YSZ ceramic were investigated. The volume erosion rate raised and developed a nonlinear dependence on the weight of corundum abrasive particles at room temperature. The slope of the curve decreased gradually. At elevated temperature, volume erosion rate increased as the temperature went up. Nonlinear fitting presents the relationship between the volume erosion rate of 3YSZ ceramics and the corresponding temperature. Plastic deformation is the major erosion mechanism at room temperature when the weight of corundum particles was 300g and 900g. Minor chipping instead of it when the temperature grew up to 400 and 600°C or the corundum particles was as much as 1800g at 25°C. When 3YSZ targets were eroded at 800°C and 1000°C, the material removal are mainly attributed to lateral cracks for an ideally brittle material. Crack propagation is the controlling factor of volume erosion rate.

Solid Particle Erosion-Wear Behavior of Mullite-SiC-Sialon Composite Wear-Resistant Refractories at High-temperature

Solid Particle Erosion-Wear Behavior Of Sic-Sialon Composite Refractories At High-Temperature

Effect of Silicon Addition on High-Temperature Solid Particle Erosion-Wear Behaviour of Mullite-SiC Composite Refractories Prepared by Nitriding Reactive

Solid Particle Erosion-Wear Behavior of SiC–Si 3 N 4 Composite Ceramic at Elevated Temperature

Solid Particle Erosion Behavior of High Alumina Refractory at Elevated Temperatures

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Reaction Sintered Fe–Sialon Ceramic Composite: Processing, Characterization and High Temperature Erosion Wear Behavior

Solid Particle Impact Erosion of Alumina-Based Refractories at Elevated Temperatures

Solid Particle Erosion-Wear Behavior of Alumina Ceramics at High-Temperature

Solid Particle Erosion Behavior of 3YSZ Ceramics at Elevated Temperatures

Abrasive wear behavior of SiCp–Sialon composite refractories

Erosion Wear Behaviour of 3 Mol-% Yttria-Stabilised Zirconia Ceramics by Solid Particle Impact at Elevated Temperatures

Ablation behavior and mechanisms of 3D C<sub>f</sub>/ZrB<sub>2</sub>-SiC composite applied in long-term temperature up to 2400 C

Mechanical Properties and Solid Particle Erosion Behavior of LaMgAl11O19–Al2O3 Ceramic at Room and Elevated Temperatures

Solid particle erosion of alumina ceramics at elevated temperature

Study of Erosion Wear Behavior of MgO Stabilized ZrO2 Ceramics Due to Solid Particles Impact at Elevated Temperature

Hot strength and microstructure of β-sialon-Al2O3-SiC composites

Ablation behavior and mechanisms of 3D Cf/ZrB2-SiC composite applied in long-term temperature up to 2400 °C

Fabrication and properties of Al 2O 3-SiC/Sialon composite refractories

Fabrication and Properties of Al<sub>2</sub>O<sub>3</sub>-SiC/Sialon Composite Refractories

Erosion behavior between CaCl2 and β-Sialon -SiC composite used for blast furnaces