Abstract:The current available wood-plastic materials used for selective laser sintering (SLS) investment casting are often poor in fluidity in molten state, which is not easy to flow out the shell mold. This led to a large amount of residual ash in mold after heating and lowered the quality of the sintered parts. In this article, the Co-Polyamide (Co-PA Hotmelt adhesive) and rice husk powders (RH) were proposed as the feedstock of the rice husk (RH)/CO-PA composite (RHPA) for SLS. CO-PA with good fluidity was used as the matrix and RH powder as the additive materials. This paper aims to optimize the SLS processing parameters and determine the optimal ratio of RHPA parts manufactured by SLS. Through this work, an orthogonal experimental method of five factors and four levels was used to determine the optimum SLS parameters for the RHPA SLS test. The scan spacing, scan speed, laser power, layer thickness, and preheating temperature are chosen as main SLS affecting factors of this study. The synthesis weighted scoring methods were used to conclude the optimal combination of SLS parameters of RHPA i.e., scan spacing = 0.15mm, scan speed = 2m/s, laser power =16W, layer thickness = 0.25 mm and the preheating temperature = 74°C. Moreover, the influence of RH content on the mechanical properties, dimensional accuracy, and the residual ash content of RHPA parts was determined. When the ratio of RH powder on RHPA is 10 wt %, the bending strength of the sintered parts will reach 2 MPa. Besides, the residual ash content of RHPA parts after heating step was lower (1.1881%) and the tolerance level is CT5. Thus, the dimensional accuracy in X, Y, and Z directions of 10 wt % RHPA SLS parts is 99.79%, 98.71%, and 97.9%, respectively; and the surface of casting was smooth and clear details.

Study on Densification of Al2O3-Polymer Composite Powders via Indirect Selective Laser Sintering Combined with Isostatic Pressing

Densification of Alumina Components Via Indirect Selective Laser Sintering Combined with Isostatic Pressing

Indirect Selective Laser Sintering of Epoxy Resin-Al2o3 Ceramic Powders Combined with Cold Isostatic Pressing

Investigation into Indirect Selective Laser Sintering Alumina Ceramic Parts Combined with Cold Isostatic Pressing

Properties of Alumina Green Parts via Selective Laser Sintering Combined with Cold Isostatic Pressing

Additive Manufacturing of Traditional Ceramic Powder Via Selective Laser Sintering with Cold Isostatic Pressing

Numerical Simulation of Cold Isostatic Pressed Alumina Parts Produced by Selective Laser Sintering and Part Shape Optimization

Compound process of selective laser processed alumina parts densified by cold isostatic pressing and solid state sintering: Experiments, full process simulation and parameter optimization

Experimental Based Full Process Simulation of Alumina Selective Laser Processed Parts Densified by Cold Isostatic Pressing and Solid State Sintering

Technology and simulation of cold isostatic pressing of selective laser sintered parts

Research on selective laser sintering of Kaolin–epoxy resin ceramic powders combined with cold isostatic pressing and sintering

Densification of Porous Stainless-Steel SLS Components During Cold Isostatic Pressing

Study on selective laser sintering process and investment casting of rice husk/ Co-Polyamide (Co-PA hotmelt adhesive) composite

Investigation into the Densification of AISI 304 Parts Fabricated by Hybrid Powder Metallurgy Techniques

Characterisation of Samples from Fe Based Composite Materials Prepared by Different Powder Metallurgy Techniques

Sintering Densification of Cu/Al2O3p Nano-Composite Powders by Electroless Copper Plating

Towards Fabrication of High-Performance Al2O3 Ceramics by Indirect Selective Laser Sintering Based on Particle Packing Optimization

Al2O3/SiO2 composite ceramic parts by selective laser sintering

Plastic forming simulations of cold isostatic pressing of selective laser sintered components

Selective laser sintering of Si3N4 and Al 2O3 ceramic powders

Laser Additive Manufacturing and Homogeneous Densification of Complicated Shape SiC Ceramic Parts