Enhancing Mechanical Properties and Electrochemical Behavior of Equiatomic FeNiCoCr High-Entropy Alloy through Sintering and Hot Isostatic Pressing for Binder Jet 3D Printing
Ling Chen,Zhiqiang Fu,Weiping Chen,Zhiping Chen,Wei Xiong,Dezhi Zhu,Enrique J. Lavernia
DOI: https://doi.org/10.1016/j.addma.2024.103999
IF: 11
2024-01-26
Additive Manufacturing
Abstract:This study investigates the influence of sintering temperature and hot isostatic pressing (HIP) on the microstructure, mechanical properties, and electrochemical behavior of equiatomic FeNiCoCr high-entropy alloy (HEA) samples produced via binder jet 3D printing (BJ3DP). Green samples with a relative density of approximately 59.3 ± 0.4% were initially printed using pre-alloyed powders. Subsequently, sintering was performed at temperatures ranging from 1410 to 1440 °C for 4 h with an interval of 10 °C. The sintered samples exhibited a single face-centered cubic phase, and their relative densities increased with higher sintering temperatures, reaching values of approximately 78.1%, 88.3%, 91.0%, and 98.1% for temperatures of 1410, 1420, 1430, and 1440 °C, respectively. The effect of hot isostatic pressing (HIP) at 1200 °C under a pressure of 150 MPa for 2 h in an argon atmosphere was found to be minimal for samples with relative densities below 91.0%. However, HIP substantially enhanced both the densities and mechanical properties for samples with relative densities of 91.0% or higher. The samples sintered at 1440 °C (#S1440) displayed the optimal mechanical properties, i.e., the values of yield strength ( σ y ), ultimate tensile strength ( σ UTS ), and total elongation ( ε t ) are ~173 MPa, ~476 MPa, and ~41%, respectively. Further processing #S1440 sample using HIP at 1200 °C (noted as #S1440H) led to an improved relative density to ~99.4%, along with enhanced strength and ductility. Electrochemical testing in a 3.5 wt.% NaCl solution demonstrated superior performance of the #S1440H sample compared to wrought 316 L stainless steel (SS), although it exhibited slightly lower corrosion resistance compared to #S1440 due to coarser grains. X-ray photoelectron spectroscopy (XPS) analyses identified the formation of Co(Fe,Cr) 2 O 4 in the passive film, contributing to the improved corrosion resistance of FeCoNiCr.
engineering, manufacturing,materials science, multidisciplinary