Abstract:The current available wood-plastic materials used for selective laser sintering (SLS) investment casting are often poor in fluidity in molten state, which is not easy to flow out the shell mold. This led to a large amount of residual ash in mold after heating and lowered the quality of the sintered parts. In this article, the Co-Polyamide (Co-PA Hotmelt adhesive) and rice husk powders (RH) were proposed as the feedstock of the rice husk (RH)/CO-PA composite (RHPA) for SLS. CO-PA with good fluidity was used as the matrix and RH powder as the additive materials. This paper aims to optimize the SLS processing parameters and determine the optimal ratio of RHPA parts manufactured by SLS. Through this work, an orthogonal experimental method of five factors and four levels was used to determine the optimum SLS parameters for the RHPA SLS test. The scan spacing, scan speed, laser power, layer thickness, and preheating temperature are chosen as main SLS affecting factors of this study. The synthesis weighted scoring methods were used to conclude the optimal combination of SLS parameters of RHPA i.e., scan spacing = 0.15mm, scan speed = 2m/s, laser power =16W, layer thickness = 0.25 mm and the preheating temperature = 74°C. Moreover, the influence of RH content on the mechanical properties, dimensional accuracy, and the residual ash content of RHPA parts was determined. When the ratio of RH powder on RHPA is 10 wt %, the bending strength of the sintered parts will reach 2 MPa. Besides, the residual ash content of RHPA parts after heating step was lower (1.1881%) and the tolerance level is CT5. Thus, the dimensional accuracy in X, Y, and Z directions of 10 wt % RHPA SLS parts is 99.79%, 98.71%, and 97.9%, respectively; and the surface of casting was smooth and clear details.

Investigation into Indirect Selective Laser Sintering Alumina Ceramic Parts Combined with Cold Isostatic Pressing

Influence of Silicon Carbide on Direct Powder Bed Selective Laser Process (Sintering/Melting) of Alumina

Additive Manufacturing and Characterization of Complex Al2o3 Parts Based on A Novel Stereolithography Method

Preparation of Ti2AlC through in-situ selective laser forming and reaction sintering

Study of alumina ceramic parts fabricated via DLP stereolithography using powders with different sizes and morphologies

Study on selective laser sintering process and investment casting of rice husk/ Co-Polyamide (Co-PA hotmelt adhesive) composite

Evolution of the microstructure and mechanical properties of stereolithography formed alumina cores sintered in vacuum

Effects of AlN inorganic binder on the properties of porous Si3N4 ceramics prepared by selective laser sintering

The preparation of ZrO2-Al2O3 composite ceramic by SLA-3D printing and sintering processing

Fabrication of alumina ceramics with high flexural strength using stereolithography

Selective laser sintering of Si3N4 and Al 2O3 ceramic powders

Effects of raw material ratio and post-treatment on properties of soda lime glass-ceramics fabricated by selective laser sintering

Microstructure Evolution and Mechanical Properties of Ceramic Shell Moulds for Investment Casting of Turbine Blades by Selective Laser Sintering

Fabrication and characterization of SiC/Al composites prepared by laser powder bed fusion (LPBF) combined with vacuum pressure infiltration

Effect of Holding Time During Sintering on Microstructure and Properties of 3D Printed Alumina Ceramics

New Laser Machining Technology of Al2O3 Ceramic with Complex Shape

Influence of sintering temperature and CVI time on mechanical properties of 3D-printed alumina ceramics

Reinforcement effect in printing precision and sintering performance for liquid crystal display stereolithography additive manufacturing of alumina ceramics

Near-net shaping of laminated Al/Al2O3 composites by direct ink writing and pressure infiltration

Microstructure evolution and mechanical properties of Al-Al2O3 composites fabricated by selective laser melting

Directly fabricated Al2O3/GdAlO3 eutectic ceramic with large smooth surface by selective laser melting: Rapid solidification behavior and thermal field simulation