Abstract:Four carbon/carbon composites with densities of 1.75–1.81 g/cm3were produced with matrix carbons derived from (a)coal tar pitch and furfural acetone resin by impregnation-carbonization, (b) natural gas by isothermal chemical vapor infiltration and (c) xylene by film-boiling chemical vapor infiltration. Theirmechanical properties and thermal conductivities (TC) were compared and correlated to the matrix carbon microstructures. Results showed that the strength of the composites decreased as thecarbon matrix changed from natural gas pyrocarbon (PyCN), to resin-derived carbon, to xylene PyC (PyCX), and to pitch-derived carbon. The highest flexural and interlaminar shear strengths of 208.7 and 26.4MPa, respectively, were obtained for the PyCN matrix. The large amount of fiber pull-out and step-like matrix fracture contributed to a high toughness of composites with PyCN and PyCX matrices. Relatively low strength and toughness were obtained for the pitch-derived carbon. The change of TC with the matrix type was consistent with the graphitization degree and apparent crystallite height. The highest in-plane and out-of-plane TC reached 148.2 and 75.4 W/(m·K), respectively, for the PyCX matrix, which was due to its carbon layers having the highest preferred orientation. The chaotic structure and large number of defects of the resin-derived carbon produced a relatively low TC. PyCN was the most suitable matrix for composites with excellent mechanical properties. PyCXshould be used to improve the TC and toughness of the low-cost composites.

Optimizing Mechanical and Thermal Expansion Properties of Carbon/carbon Composites by Controlling Textures

Microstructure and Mechanical Properties of Multilayer-textured 2D Carbon/Carbon Composites

Preparation and Mechanical Properties of Carbon/carbon Composites with High Textured Pyrolytic Carbon Matrix

Variation of Thermal Expansion of Carbon/carbon Composites from 850 to 2500°C

Effect of pyrolysised carbon content on properties of C/C composites

Thermophysical Properties of Carbon/carbon Composites and Physical Mechanism of Thermal Expansion and Thermal Conductivity

Realizing the synergy of carbon nanotubes and matrix microstructure for improved flexural behavior of laminated carbon/carbon composites

Variation of thermal expansion of carbon/carbon composites from 850 to 2500 °C

Effect of High Temperature Treatment on the Microstructure and Mechanical Properties of Binary Layer Textured 2d C/C Composites

Influence of the matrix texture on the fracture behavior of 2D carbon/carbon composites

Dependence of Mechanical Properties on Microstructure of High-Textured Pyrocarbon Prepared Via Isothermal and Thermal Gradient Chemical Vapor Infiltration

Mechanical and thermal conduction properties of carbon/carbon composites with different carbon matrix microstructures

The thermal expansion behavior of 3D C/C composites

Effect of pyrocarbon interphase texture and thickness on tensile damage and fracture in T‐700TM carbon fiber–reinforced silicon carbide minicomposites

Potential of Porous Pyrolytic Carbon for Producing Zero Thermal Expansion Coefficient Composites: A Multi-Scale Numerical Evaluation

Study on the Thermal Expansion Properties of C/C Composites

Thermal Expansion Property of Carbon/carbon Composite

Effects of preform and pyrolytic carbon structure on thermophysical properties of 2D carbon/carbon composites

Multi-scale Modeling of Thermal Expansion Coefficients of C/C Composites at High Temperature

Effect of Pyrocarbon Interphase Texture and Thickness on Tensile Damage and Fracture in T‐700™ Carbon Fiber–reinforced Silicon Carbide Minicomposites

Effect of Heat Treatment on the Microstructure of C/C Composites with Different High Textured Pyrolytic Carbon Contents