Abstract:AlN-SiC solid solution particles with a variety of morphologies including faceted polyhedrons with or without ledges; hexagonal platelets; hexagonal columns with a hexagonal plate or a pyramidal cap; and interpenetrating cones, have been found in the combustion products of a mixture of Al, Si, and carbon black under a nitrogen pressure of 10 MPa. Combustion temperature (the growth temperature of crystals) is the most important factor controlling the morphology of crystals formed in the combustion product. When temperatures are close to the melting point of the solid solutions, a small driving force for nucleation and long distances of surface migration make nucleation on the basal plane difficult, and thus the solid solution particles tend to grow as platelets. Supersaturation is the second key factor influencing crystal growth. At relatively low temperatures, a low supersaturation at the large pores renders nucleation difficult and the solid solution particles tend to grow as platelets. At relatively low temperatures and high supersaturation, a relatively high driving force for nucleation and short mean distances of surface migration promote the growth of AlN-SiC solid solutions as polyhedrons. The formation of the ledges on the polyhedral particles is attributed to the differences in the evaporation rates and the deposition rates between Al and Si. At relatively low temperatures and an intermediate supersaturation, the solid solution particles grow as prismatic columns. The formation of the prismatic columns with a hexagonal plate, or a pyramidal cap, is attributed to a sudden change of temperature during combustion. A possible growth mechanism for the AlN-SiC solid solution cones is proposed.

Synthesis and Growth of 6H-Sic and 3C-Sic in an Al–Si–C System at 820 °C: Effect of the Reaction Path on the SiC Polytype

In-situ synthesis of nano SiC particles in Al–Si–C system at 750 °C

Characterization of 4H-Sic Grown on AlN/Si(100) by CVD

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Controlled growth of SiC crystals in combustion synthesis

Growth Mechanisms for SiC-AlN Solid Solution Crystals Prepared by Combustion Synthesis

Growth of 4H-Sic on AlN/Si(100) Complex Substrate by Chemical Vapor Deposition

Effect of C/Si Ratio on the Characteristics of 3C-Sic Films Deposited on Si(100) Base on the Four-Step Non-Cooling Process

Synthesis, characterization and growth mechanism of SiC fibers

Synthesis and investigation of the physicochemical properties of polymorphic 3C–SiC

The Growth of Si on Sic Complex Substrate by Cvd

The Growth of Sic Crystals from Cosi Molten Alloy Fluxes

Combustion synthesis of SiC/Al2O3 composite powders with SiC nanowires and their growth mechanism

Combustion synthesis of AlN-SIC solid solutions

Syntheses and Growth Mechanisms of 3C-Sic Nanostructures from Carbon and Silicon Powders.

Synthesis of High Purity SiC Powder for High-resistivity SiC Single Crystals Growth

Layered Growth Modelling of Epitaxial Growth Processes for SiC Polytypes

Synthesis of SiC-AlN Ceramic Alloy Powder by the Direct Reactions Between the Constituent Elements.

SiC Crystal Growth from Transition Metal Silicide Fluxes

In Situ Reactive Synthesis and Phase Stability Investigation in the AlN-SiC System

The growth of Si1-yCy alloy on 6H-SiC homoepitaxial layers