Abstract:Herein, triethanolamine additive is innovatively utilized to regulate the hydrothermal process of Sb2(S,Se)3 thin film. Ultimately, the longitudinal Se/(S+Se) ratio of Sb2(S,Se)3 thin film is well controlled. The enhanced vertical crystal orientations, the uniformed back surface gradient, the suppressed over band bending at PN junction and the passivated harmful VSe1 defects leading to an efficiency of 9.94% for Sb2(S,Se)3 solar cell. Antimony selenosulfide (Sb2(S,Se)3) solar cells have achieved an efficiency of over 10.0%. However, the uncontrollable hydrothermal process makes preparing high‐quality Sb2(S,Se)3 thin films a bottleneck for efficient Sb2(S,Se)3 solar cell. To address this problem, triethanolamine (TEA) additive is innovatively utilized to regulate the reaction kinetic process of Sb2(S,Se)3 thin films in this work. The results show that TEA chelator can realize the time‐domain control of the reaction process, optimizing the Se/(S+Se) elemental distribution of Sb2(S,Se)3 thin film and shrinking the bandgap offset of Sb2(S,Se)3 thin film. Meanwhile, the (021) and (061) crystal orientation of Sb2(S,Se)3 thin film are enhanced and the harmful VSe1 defects in Sb2(S,Se)3 solar cells are passivated. Interestingly, a uniform back surface gradient for Sb2(S,Se)3 thin film is formed to reduce the minority carrier recombination at the back contact, increase the photocurrent and decrease the diode current of Sb2(S,Se)3 solar cells. Finally, the Jsc and FF of Sb2(S,Se)3 solar cells are significantly improved by 8.6% and 5.5% respectively, and the open‐circuit voltage deficit of the device is reduced by 44 mV, which leads to an efficiency of 9.94% which is the highest values of Sb2(S,Se)3 solar cells by sodium selenosulfate system.

Efficiency Enhancement of Sb2se3 Thin-Film Solar Cells by the Co-Evaporation of Se and Sb2se3

Selenization of Sb2se3 Absorber Layer: an Efficient Step to Improve Device Performance of Cds/Sb2se3 Solar Cells

Magnetron Sputtered Sb2Se3-based Thin Films Towards High Performance Quasi-Homojunction Thin Film Solar Cells

Fabricating over 7%-efficient Sb2(S,Se)3 thin-film solar cells by vapor transport deposition using Sb2Se3 and Sb2S3 mixed powders as the evaporation source

Chemical Etching Induced Surface Modification and Gentle Gradient Bandgap for Highly Efficient Sb2(S,Se)3 Solar Cell

Thermal Diffused Post-Selenization for Enhancing the Photovoltaic Performance of Thermally Evaporated Sb2Se3 Solar Cell

Thermal diffused post-selenization for enhancing the photovoltaic performance of thermally evaporated Sb 2 Se 3 solar cell

Sequential Coevaporation and Deposition of Antimony Selenosulfide Thin Film for Efficient Solar Cells

Sb-2(Se1-xSx)(3) Thin-Film Solar Cells Fabricated by Single-Source Vapor Transport Deposition

Efficiency Enhancement of Sb2Se3 Solar Cells Based on Electron Beam Evaporation CdS Film with Variable Deposition Temperature

Fabricating High‐Efficiency Sb2(S,Se)3 Solar Cells by Novel Additive‐Assisted Longitudinal Component Engineering

Sb2Se3 Solar Cells Fabricated Via Close-Space Sublimation

Achievable efficiency improvement of Sb2Se3 thin-film solar cells through interface engineering

Co‐Evaporated CuSbSe2 Thin Films for Solar Cells

Sb2Se3 thin film solar cells in substrate configuration and the back contact selenization

An effective combination reaction involved with sputtered and selenized Sb precursors for efficient Sb2Se3 thin film solar cells

Improving the Performance of Sb2Se3 Thin Film Solar Cells over 4% by Controlled Addition of Oxygen During Film Deposition

Single-source Thermal Evaporation Converts Anion Controllable Sb 2 (s,se) 3 Film for Fabricating High-Efficiency Solar Cell

Solvent‐Assisted Hydrothermal Deposition Approach for Highly‐Efficient Sb2(S,Se)3 Thin‐Film Solar Cells

Improved Open‐Circuit Voltage of Sb2Se3 Thin‐Film Solar Cells Via Interfacial Sulfur Diffusion‐Induced Gradient Bandgap Engineering

Optimisation of Sb2S3 thin-film solar cells via Sb2Se3 post-treatment