Abstract:Herein, triethanolamine additive is innovatively utilized to regulate the hydrothermal process of Sb2(S,Se)3 thin film. Ultimately, the longitudinal Se/(S+Se) ratio of Sb2(S,Se)3 thin film is well controlled. The enhanced vertical crystal orientations, the uniformed back surface gradient, the suppressed over band bending at PN junction and the passivated harmful VSe1 defects leading to an efficiency of 9.94% for Sb2(S,Se)3 solar cell. Antimony selenosulfide (Sb2(S,Se)3) solar cells have achieved an efficiency of over 10.0%. However, the uncontrollable hydrothermal process makes preparing high‐quality Sb2(S,Se)3 thin films a bottleneck for efficient Sb2(S,Se)3 solar cell. To address this problem, triethanolamine (TEA) additive is innovatively utilized to regulate the reaction kinetic process of Sb2(S,Se)3 thin films in this work. The results show that TEA chelator can realize the time‐domain control of the reaction process, optimizing the Se/(S+Se) elemental distribution of Sb2(S,Se)3 thin film and shrinking the bandgap offset of Sb2(S,Se)3 thin film. Meanwhile, the (021) and (061) crystal orientation of Sb2(S,Se)3 thin film are enhanced and the harmful VSe1 defects in Sb2(S,Se)3 solar cells are passivated. Interestingly, a uniform back surface gradient for Sb2(S,Se)3 thin film is formed to reduce the minority carrier recombination at the back contact, increase the photocurrent and decrease the diode current of Sb2(S,Se)3 solar cells. Finally, the Jsc and FF of Sb2(S,Se)3 solar cells are significantly improved by 8.6% and 5.5% respectively, and the open‐circuit voltage deficit of the device is reduced by 44 mV, which leads to an efficiency of 9.94% which is the highest values of Sb2(S,Se)3 solar cells by sodium selenosulfate system.

Achievable efficiency improvement of Sb2Se3 thin-film solar cells through interface engineering

Solution-processed SnO2 interfacial layer for highly efficient Sb2Se3 thin film solar cells

Interfacial engineering for high efficiency solution processed Sb2Se3 solar cells

Heterojunction Interface Engineering of C60 Electron Transport Layer Insertion Enables Efficient Cd-Free Sb2se3 Solar Cells

An effective engineering with simultaneous carrier density enhancement and interface optimization enables efficient Sb2Se3 solar cells

Interfacial Engineering Towards Enhanced Photovoltaic Performance of Sb2Se3 Solar Cell

ZnxCd1–xSySe1–y as an effective electron transport layer for improving the efficiency of Sb2S3 and Sb2Se3 thin-film solar cells

Efficiency Enhancement of Sb2se3 Thin-Film Solar Cells by the Co-Evaporation of Se and Sb2se3

High-efficient Sb 2 Se 3 solar cell using Zn x Cd 1- x S n-type layer

Optimisation of Sb2S3 thin-film solar cells via Sb2Se3 post-treatment

Interfacial Engineering by Applying Double CdS Structure Electron Transport Layer for High-Performance Sb2(S,Se)3 Solar Cells

Efficiency Improvement of Flexible Sb2Se3 Solar Cells with Non-Toxic Buffer Layer Via Interface Engineering

Chemical Etching Induced Surface Modification and Gentle Gradient Bandgap for Highly Efficient Sb2(S,Se)3 Solar Cell

Fabricating High‐Efficiency Sb2(S,Se)3 Solar Cells by Novel Additive‐Assisted Longitudinal Component Engineering

Double Interface Modification Promotes Efficient Sb2Se3 Solar Cell by Tailoring Band Alignment and Light Harvest

Towards high efficiency inverted Sb2Se3 thin film solar cells

Stable and Efficient CdS/Sb2Se3 Solar Cells Prepared by Scalable Close Space Sublimation

Electron Transport Layer Engineering Induced Carrier Dynamics Optimization for Efficient Cd-Free Sb2 Se3 Thin-Film Solar Cells.

Plasma Etching-Induced Surface Modification and Interfacial Defect Passivation for Antimony Triselenide Thin Film Solar Cells

Remarkable Cd-free Sb<sub>2</sub>Se<sub>3</sub> solar cell yield achieved by interface band-alignment and growth orientation screening

Suppressing Buried Interface Nonradiative Recombination Losses Towards High‐efficiency Antimony Triselenide Solar Cells