Abstract:Herein, triethanolamine additive is innovatively utilized to regulate the hydrothermal process of Sb2(S,Se)3 thin film. Ultimately, the longitudinal Se/(S+Se) ratio of Sb2(S,Se)3 thin film is well controlled. The enhanced vertical crystal orientations, the uniformed back surface gradient, the suppressed over band bending at PN junction and the passivated harmful VSe1 defects leading to an efficiency of 9.94% for Sb2(S,Se)3 solar cell. Antimony selenosulfide (Sb2(S,Se)3) solar cells have achieved an efficiency of over 10.0%. However, the uncontrollable hydrothermal process makes preparing high‐quality Sb2(S,Se)3 thin films a bottleneck for efficient Sb2(S,Se)3 solar cell. To address this problem, triethanolamine (TEA) additive is innovatively utilized to regulate the reaction kinetic process of Sb2(S,Se)3 thin films in this work. The results show that TEA chelator can realize the time‐domain control of the reaction process, optimizing the Se/(S+Se) elemental distribution of Sb2(S,Se)3 thin film and shrinking the bandgap offset of Sb2(S,Se)3 thin film. Meanwhile, the (021) and (061) crystal orientation of Sb2(S,Se)3 thin film are enhanced and the harmful VSe1 defects in Sb2(S,Se)3 solar cells are passivated. Interestingly, a uniform back surface gradient for Sb2(S,Se)3 thin film is formed to reduce the minority carrier recombination at the back contact, increase the photocurrent and decrease the diode current of Sb2(S,Se)3 solar cells. Finally, the Jsc and FF of Sb2(S,Se)3 solar cells are significantly improved by 8.6% and 5.5% respectively, and the open‐circuit voltage deficit of the device is reduced by 44 mV, which leads to an efficiency of 9.94% which is the highest values of Sb2(S,Se)3 solar cells by sodium selenosulfate system.

Towards high efficiency inverted Sb2Se3 thin film solar cells

Magnetron Sputtered Sb2Se3-based Thin Films Towards High Performance Quasi-Homojunction Thin Film Solar Cells

Solution-processed SnO2 interfacial layer for highly efficient Sb2Se3 thin film solar cells

Stable and efficient Sb2Se3 solar cells with solution-processed NiOx hole-transport layer

Interfacial engineering for high efficiency solution processed Sb2Se3 solar cells

Achievable efficiency improvement of Sb2Se3 thin-film solar cells through interface engineering

Highly Efficient and Stable Planar Heterojunction Solar Cell Based on Sputtered and Post-Selenized Sb 2 Se 3 Thin Film

Highly efficient and stable planar heterojunction solar cell based on sputtered and post-selenized Sb2Se3 thin film

Optimizing Crystal Orientation and Defect Mitigation in Antimony Selenide Thin-Film Solar Cells through Buffer Layer Energy Band Adjustment

Suppressing Buried Interface Nonradiative Recombination Losses Towards High‐efficiency Antimony Triselenide Solar Cells

An Optimization Path for Sb2(S,Se)3 Solar Cells to Achieve an Efficiency Exceeding 20

Temperature‐Gradient Solution Deposition Amends Unfavorable Band Structure of Sb2(S,Se)3 Film for Highly Efficient Solar Cells

Interface engineering of antimony selenide solar cells: A review on the optimization of energy band alignments

Efficiency Improvement Of Sb2se3 Solar Cells Via Grain Boundary Inversion

Enhancement in the efficiency of Sb2(S,Se)3 thin-film solar cells with Spin-coating NiOx as the hole transport layer

An effective engineering with simultaneous carrier density enhancement and interface optimization enables efficient Sb2Se3 solar cells

Enhanced charge carrier transport via efficient grain conduction mode for Sb2Se3 solar cell applications

Fabricating High‐Efficiency Sb2(S,Se)3 Solar Cells by Novel Additive‐Assisted Longitudinal Component Engineering

High-efficiency and stable Sb2(S,Se)3 thin film solar cells with phthalocyanine as a hole transport layer

Regulating Energy Band Alignment via Alkaline Metal Fluoride Assisted Solution Post‐Treatment Enabling Sb 2 (S,Se) 3 Solar Cells with 10.7% Efficiency

High-efficient Sb 2 Se 3 solar cell using Zn x Cd 1- x S n-type layer