Abstract:For high transparent materials, the difference among the transmittances of various slabs in different thicknesses is very slight since the index of absorption is rather small. However, the divergence of transmittances is very necessary to provide multiple independent constraints for retrieving spectral intrinsic properties from transmitted data with an acceptable accuracy. A Multi-Layer-Combination (MLC) method in which multiple sheets compose a transmitted combination is proposed to provide obviously different transmittances. In this study, the measurements on MLC slabs of C-plane sapphire were performed between 0.8 and 7.0 mu m from room temperature to 1800 K. For a given total thickness, the measured results show that the stacking structure of multiple layers can obviously diminish the transmittance, but has no influence on the infrared cutoff and infrared border of high transparency. The spectral refractive indexes and absorption indices within 0.8-5 mu m were extracted from transmittance data by minimizing the standard deviation between measurements and predictions. The results indicate that all the properties are wavelength dependent and temperature dependent. Spectral refractive indexes rise regularly with growing temperature and decrease slowly with increasing wavelength. For a researched temperature, the index of absorption levels off in the high transparent interval and climbs steadily in the next spectrum as the wavelength increases. In the tested temperature range of 300-1800 K, the spectral absorption indices rise gradually with increasing temperature. The absorption edge moves forward to the short wavelength infrared from about 3.5 mu m at 300 K to about 2.75 mu m at 1800 K. (C) 2018 Elsevier Ltd. All rights reserved.

Multi-phonon interaction of ZnS material based on two-dimensional correlation analysis

Physical Model of the Infrared Dielectric Function of Zinc Sulfide

Parameters inversion of ZnS multi-phonon absorption model based on the transmissivities in variable temperature

Measurement Method for High-Temperature Infrared Optical Constants of ZnS Crystal Materials in a Multi-Layer Structure

The Optical Properties of ZnS Dependent on Different Fabricating Process

ZnS fabricated by spark plasma sintering and its properties

Temperature Dependence of Phonon Modes, Dielectric Functions, and Interband Electronic Transitions in Cu2ZnSnS4 Semiconductor Films

Far-Infrared Characteristics of Zns Nanoparticles Measured by Terahertz Time-Domain Spectroscopy

Spectral Emissivity and Transmissivity Measurement for Zinc Sulphide Infrared Window Based on Integrating-Sphere Reflectometry

First-principles study of mechanical and optical properties for ZnS<sub>1<i>-x</i></sub>O<i><sub>x</sub></i> alloying compounds

Crystal Structures, Lattice Vibrational Characteristics, and Dielectric Responses of Znwo4 Microwave Dielectric Ceramics Sintered at Different Temperatures

Optical interband transitions in Zn2TiO4 single crystals

First-principles study of mechanical and optical properties for ZnS1−O alloying compounds

Fabrication of an Anti-Reflective Microstructure on ZnS by Femtosecond Laser Bessel Beams

Temperature Measurements of High-Temperature Semi-Transparent Infrared Material Using Multi-Wavelength Pyrometry

Preparation and Protection of ZnS Surface Sub-Wavelength Structure for Infrared Window

The Phase Structure of ZnS Bulk Materials Prepared by Chemical Vapor Deposition

Infrared transmission spectra of Cd 1−x Zn x Te (x = 0.04) crystals

Long-Wavelength Optical Phonon Properties Of Ternary Mgzno Thin Films

Multi-layer-combination Method to Retrieve High-Temperature Spectral Properties of C-plane Sapphire

Rapid Heating Thermal Shock Behavior Study of CVD ZnS Infrared Window Material: Numerical and Experimental Study