Abstract:Magnesium aluminate (MgAl2O4) spinel has grasped considerable attention in high-temperature application by right of its excellent properties. However, the poor sintering behavior of MgAl2O4 is detrimental to its further development. In the present work, the application of isostructural heterogeneous nucleation method provides a novel idea for optimizing the sintering behavior of refractory materials. A series of (1-x)MgAl2O4-xMg2TiO4 (x = 0, 0.02, 0.04, 0.06, 0.08, and 0.1) spinel solid solutions with a present ration of components were fabricated from light calcined magnesia, reactive alumina and pre-preparation Mg2TiO4. The effect of Mg2TiO4 heterogeneous nucleating agent on the crystalline phase, densification, and microstructure evolution of MgAl2O4–Mg2TiO4 spinel solid solutions was studied. The XRD, XPS, and EDS results showed that Mg2TiO4 entered the lattice of MgAl2O4 to form a spinel solid solution, and the heterovalent substitution process was identified, where Ti4+ and Mg2+ ions of larger radius in the Mg2TiO4 replaced the Al3+ of smaller radius in the MgAl2O4. For the sample at x = 0.08, the spinel solid solutions exhibited the optimized densification with a relative density of 93.3%, an apparent porosity of 1.2%, and a compressive strength of 84.5 MPa. A significant increase in densification was related to the lattice distortion induced by ion size mismatch during the heterovalent substitution, thus accelerating the diffusion rate of Mg2+ and Al3+ ions in the spinelisation state. Moreover, the solid solubility content of Ti4+ in the MgAl2O4–Mg2TiO4 spinel solid solutions had a significant effect on the grain morphologies. The Mg2TiO4 heterogeneous nucleating agent significantly increased the spinelisation rate of MgAl2O4 spinel with negligible effect on densification.

Preparation of nickel aluminate spinel by solid state reaction

The effects of sintering temperature and reactive material ratio on the productivity of nickel aluminate spinel

Study on NiO Excess in Preparing NiAl2O4

Preparation and properties of Al2O3/Ni composite from NiAl2O4 spinel by in situ reaction sintering method

Combustion synthesis of NiAl2O4 spinel powder

Preparation of NiAl2O4/Al2O3 composite nanopowder

Preparation of Nanocrystalline LiMn1.90Cr0.05Ni0.05O4

Novel Synthesis of High Surface Area MgAl2O4 Spinel As Catalyst Support

Study of Preparation of Cobalt Aluminate by Sol-Gel Process and Electroless Plating

Preparation and Characterization of Novel Nonstoichiometric Magnesium Aluminate Spinels

Preparation and Electrochemical Properties of Nanocrystalline NiO

Sintering behavior and microstructure of (1-x)MgAl2O4-xMg2TiO4 spinel solid solutions prepared by isostructural heterogeneous nucleation

Preparation and Electrochemical Performance of Spinel LiAl0.08Co0.05Mn1.87O4 Cathode Materials for Long Cycle Life Lithium-ion Batteries

Preparation and Characterization of Porous Mgal2o4 Spinel Ceramic Supports from Bauxite and Magnesite

Preparation, sintering behavior and microstructure of Al2O3-Coated Ni powders

Synthesis of Zinc Aluminate Spinel Film Through the Solid‐Phase Reaction Between Zinc Oxide Film and Α‐alumina Substrate

Synthesis and Characterization of Porous Magnesium Aluminate Spinel by Hydrothermal Process

Synthesis and Characterization of Core-Shell NiO@Al2O3 with High Ni/Al Ratio and High Calcination Temperature

Effect of Temperature on the Preparation and Electrocatalytic Properties of a Spinel NiCo2O4/Ni Electrode

In situ formation mechanism of spinel-like Al5O6N and plate-like Al7O3N5 in the two-step sintered Al–Al2O3 composites

Synthesis of magnesium aluminate spinel by reaction sintering with different magnesia sources