Abstract:Magnesium aluminate (MgAl2O4) spinel has grasped considerable attention in high-temperature application by right of its excellent properties. However, the poor sintering behavior of MgAl2O4 is detrimental to its further development. In the present work, the application of isostructural heterogeneous nucleation method provides a novel idea for optimizing the sintering behavior of refractory materials. A series of (1-x)MgAl2O4-xMg2TiO4 (x = 0, 0.02, 0.04, 0.06, 0.08, and 0.1) spinel solid solutions with a present ration of components were fabricated from light calcined magnesia, reactive alumina and pre-preparation Mg2TiO4. The effect of Mg2TiO4 heterogeneous nucleating agent on the crystalline phase, densification, and microstructure evolution of MgAl2O4–Mg2TiO4 spinel solid solutions was studied. The XRD, XPS, and EDS results showed that Mg2TiO4 entered the lattice of MgAl2O4 to form a spinel solid solution, and the heterovalent substitution process was identified, where Ti4+ and Mg2+ ions of larger radius in the Mg2TiO4 replaced the Al3+ of smaller radius in the MgAl2O4. For the sample at x = 0.08, the spinel solid solutions exhibited the optimized densification with a relative density of 93.3%, an apparent porosity of 1.2%, and a compressive strength of 84.5 MPa. A significant increase in densification was related to the lattice distortion induced by ion size mismatch during the heterovalent substitution, thus accelerating the diffusion rate of Mg2+ and Al3+ ions in the spinelisation state. Moreover, the solid solubility content of Ti4+ in the MgAl2O4–Mg2TiO4 spinel solid solutions had a significant effect on the grain morphologies. The Mg2TiO4 heterogeneous nucleating agent significantly increased the spinelisation rate of MgAl2O4 spinel with negligible effect on densification.

Study on NiO Excess in Preparing NiAl2O4

PREPARATION OF NiO NANOPARTICLES ON THE SILICA SURFACE BY ADSORPTION PHASE SYNTHESIS AND ITS REGULATION ON MORPHOLOGY OF NiO PARTICLES

The effects of sintering temperature and reactive material ratio on the productivity of nickel aluminate spinel

Preparation of nickel aluminate spinel by solid state reaction

Preparation of NiAl2O4/Al2O3 composite nanopowder

Synthesis of LiNiO2 cathode materials with homogeneous Al doping at the atomic level

Combustion synthesis of NiAl2O4 spinel powder

The Effects of Alloying Elements Cr, Al, and Si on Oxidation Behaviors of Ni-Based Superalloys

Preparation and properties of Al2O3/Ni composite from NiAl2O4 spinel by in situ reaction sintering method

Enhanced Structural Stability and Oxidation Resistance of NiCoCrAlY Bonding Layer Via Al Addition

Preparation, sintering behavior and microstructure of Al2O3-Coated Ni powders

Preparation and Characterization of Novel Nonstoichiometric Magnesium Aluminate Spinels

Inhibiting the Formation of Planar Defects in Grown Alumina Scale on Ni-Al Alloys

Preparation of Nanocrystalline LiMn1.90Cr0.05Ni0.05O4

Effects of Reactive Element Oxides on the Isothermal Oxidation of Β-Nial Coatings Fabricated by Spark Plasma Sintering

Characterization of Dispersion and Surface States of NiO/γ-alumina and NiO/La2O3–γ-alumina Catalysts

Sintering behavior and microstructure of (1-x)MgAl2O4-xMg2TiO4 spinel solid solutions prepared by isostructural heterogeneous nucleation

Study on Microstructure of NiAl Matrix High Temperature Lubricating Composites Containing BaO/TiO2 Metallic Oxide

Effect of nickel content on the sintering behavior, mechanical and dielectric properties of Al2O3/Ni composites from coated powders

Role of Volatilization of Molybdenum Oxides During the Cyclic Oxidation of High-Mo Containing Ni-based Single Crystal Superalloys

Effect of Al Content on Reaction Laser Sintering of Ni-Al Powder