Abstract:Prior to practical service, hot-section components (e.g. airfoils and vanes) of a gas turbine engine are necessarily coated by a protective metallic coating (such as aluminidi diffusion coating, modified aluminide coating and MCrAlY overlay etc.) to resist high temperature oxidation and hot corrosion. Among the modified aluminide coatings, the coating with Pt-modification has attracted great attention and is widely used in applications requiring high reliability and extended service life since it possesses superior oxidation/corrosion resistance at high temperature. The presence of Pt in aluminide coating is favorable for increasing bonding strength of oxide scale, enlarging phase region of beta 3-NiAI and confining detrimental effect of sulphur etc. Although Pt-modification has exhibited visible benefits for acquiring better high-temperature performance, it is far from satisfaction to develop an ideal aluminide diffusion coating. Reactive elements such as Y, Hf, Zr or their oxides have been employed to modify the nickel aluminide coating system, with an aim to further improve scale adhesion and promote exclusive formation of alpha-Al2O3 simultaneously. In this work, a Zr-doped PtAl2+(Ni, Pt)Al dual-phase aluminide coating was prepared on a Ni-based single crystal superalloy by co-deposition of Pt-Zr through electroplating and sub-sequent aluminization treatments The coating was mainly composed of three layers: the outmost layer consisted of double phases with PtAl2 particles dispersed in beta-(Ni, Pt)Al domain, while the interlayer comprised beta-(Ni, Pt)Al with small amount of Cr-precipitates, and the bottom layer was an inter-diffusion zone (IDZ). Zirconium was mainly distributed inside beta-(Ni, Pt)Al solid solution in both the outmost layer and the interlayer. Compared with normal PtAl2+(Ni, Pt)Al dual-phase coating, the hot corrosion behavior of the Zr-doped PtAl2 + (Ni, Pt)Al coating was assessed in a salt mixture of Na2SO4/NaCI (75:25, mass ratio) at 850 degrees C in static air. The results indicated that the Zr-doped PtAl2+(Ni, Pt)Al dual-phase coating exhibited superior hot corrosion resistance since Zr was confirmed able to capture and fix S and CI to diminish their detrimental effects. Meanwhile, a pre-oxidation treatment did not effectively improve the overall hot corrosion resistance of normal PtAl2+(Ni, Pt)Al coating because the thin alumina scale formed during pre-oxidation was unable to prohibit the sustained inward-invasion of the mixed salt.

Effect of Pt-rich Position on the Hot Corrosion Behavior of NiCoCrAlY Coating for a Single-Crystal Superalloy

Effect of Pt modification on hot corrosion resistance of NiCrAlYSi+AlY coating at 900 °C

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

Hot Corrosion of Arc Ion Plating NiCrAlY and Sputtered Nanocrystalline Coatings on a Nickel-Based Single-Crystal Superalloy

Hot Corrosion Behaviour of Single-Phase Platinum-Modified Aluminide Coatings: Effect of Pt Content and Pre-Oxidation

Cyclic oxidation behavior of Pt modified NiCoCrAlYHfZr + AlNiY coating on a Ni-based single crystal superalloy

Hot Corrosion Behavior of Pt+Hf Co-Modified NiAl Coating in the Mixed Salt of Na2SO4-NaCl at 900 °C

Modification of NiCoCrAlY with Pt: Part I. Effect of Pt Depositing Location and Cyclic Oxidation Performance

High-temperature Corrosion Behaviour of Pt-modified Aluminide Coating with Solid NaCl Deposit in O2 + 10 Vol% H2O and the Influence of Pre-Oxidation Treatment

High-Temperature Corrosion Behaviour of Pt-Modified Aluminide Coating under the Effect of Nacl Plus Water Vapour and the Influence of Pre-Oxidation Treatment

High-temperature Performance of (ni,pt)al Coatings on Second-Generation Ni-base Single-Crystal Superalloy at 1100 °C: Effect of Excess S Impurities

Hot corrosion of sputtered nanocrystalline coating with and without preoxidation and arc ion plating coating on a Ni-based single-crystal superalloy

High-temperature performance of Pt-modified Ni-20Co-28Cr-10Al-0.5Y coating: Formation mechanism of Pt-rich overlayer and its effect on thermally grown oxide failure

Studies on Corrosion Behavior of a Single-Crystal Superalloy and Its Sputtered Nanocrystalline Coatings with Solid NaCl Deposit in O2 + 38 Vol.% H2O Environment at 700 °C

Influence of Pt on oxidation behavior of CoNiCrAlY alloy

Hot Corrosion and Electrochemical Behavior of NiCrAlY, NiCoCrAlY and NiCoCrAlYTa Coatings in Molten NaCl-Na2SO4 at 800 °C

Influence of Cr Content on Hot Corrosion and a Special Tube Sealing Test of Single Crystal Nickel Base Superalloy

Hot Corrosion and Cyclic Oxidation Performance of a Ptal2-Dispersed (ni,pt)al Coating Prepared by Low-Activity High-Temperature Aluminizing

A Zr-doped single-phase Pt-modified aluminide coating and the enhanced hot corrosion resistance

Preparation and Enhanced Hot Corrosion Resistance of a Zr-Doped PtAl2+(Ni, Pt)Al Dual-Phase Coating

(Invited) Benefits of Zr Addition on Hot Corrosion and Isothermal Oxidation Resistance of Single-Phase (ni,pt) Al Coatings